Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-08T17:15:22Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_EfeitoAdicoesNi.pdf: 5757867 bytes, checksum: 8a77abd3b782bdae2352df421372bf23 (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-09-01T15:39:57Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_EfeitoAdicoesNi.pdf: 5757867 bytes, checksum: 8a77abd3b782bdae2352df421372bf23 (MD5) / Made available in DSpace on 2014-09-01T15:39:57Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_EfeitoAdicoesNi.pdf: 5757867 bytes, checksum: 8a77abd3b782bdae2352df421372bf23 (MD5)
Previous issue date: 2013 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Este trabalho estudou a influência dos teores dos solutos Mg e Ni na modificação das propriedades térmicas, elétricas e mecânicas de uma liga Al-Cu-Fe para aplicação como condutor de energia elétrica. Para a realização do presente estudo, as ligas foram obtidas por
fundição unidirecional horizontal, a partir da base do alumínio de pureza comercial com
adição dos teores 0,05%p Cu e [0,24 a 0,28]%p Fe. Tal base foi modificada em uma primeira
etapa com teores de 0,45, 0,60 e 0,80%p Mg. As ligas obtidas com estes teores tiveram suas
propriedades estudadas para que se selecionasse um teor de Mg para posterior adição de Ni à liga. O estudo destas propriedades na primeira etapa passou pela análise das propriedades
térmicas: velocidade de solidificação (VL) e taxa de resfriamento (Ṫ). A caracterização elétrica estudou a propriedade condutividade elétrica (φ) e o levantamento das propriedades
mecânicas: limite de resistência à tração (σ) e microdureza Vickers (HV). A liga com adição
de Ni passou por tratamentos térmicos de envelhecimento, por 1, 4 e 8h. Estas amostras foram
analisadas em um microscópio eletrônico de varredura - MEV pelos sinais de elétrons retroespalhados
– ERE e espectroscopia de energia dispersiva – EDS. Como resultados do estudo,
encontrou-se que adições de Mg influenciaram significativamente a viscosidade das ligas,
elevando as velocidades de solidificação nos instantes finais. Os ensaios de microdureza das
amostras envelhecidas mostraram que houve um acréscimo significativo de dureza na quarta
hora de envelhecimento, da mesma forma que as análises de EDS mostraram que a
concentração de Ni também elevou-se nesta condição de tratamento. / This work studied the influence of Mg and Ni solute content on the modification of
the thermal, electrical and mechanical properties of an Al-Cu-Fe alloy for application as an
electrical conductor. To realize the present study, the alloys were obtained by unidirectional
horizontal casting, starting from the commercial pure aluminum with the addition of 0.05wt%
Cu and [0.24 to 0.28]wt% Fe content. This basis was modified on a first stage with 0.45, 0.60
and 0.80wt% of Mg content. The alloys obtained with these contents had its properties studied
for the selection of a Mg content for further Ni addition at the alloy. The study of these
properties on the first stage passed through the analysis of the thermal properties: growth rate
(VL) and cooling rate (Ṫ). The electrical characterization studied the electrical conductivity
property (φ) and the following mechanical properties were determined: ultimate tensile
strength (σ) and Vickers microhardness (HV). The alloy which has Ni additions passed
through ageing heat treatments of 1, 4 and 8 hours. These samples were analyzed in a
scanning electron microscope – SEM by the electrons backscattered – EBS and energy
dispersive spectroscopy – EDS signals. As a result of the research, it was found that Mg
additions had significantly influenced the alloys viscosity, increasing its growth rates at the
final moments of the solidification. The microhardness tests for the aged samples showed that
they suffered a significant gain of hardness at the fourth hour of ageing, also, the EDS
analysis showed that Ni content increased at the same treating conditions.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5567 |
| Date | January 2013 |
| Creators | SOUZA, Pedro Henrique Lamarão |
| Contributors | QUARESMA, José Maria do Vale |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds