The aim of this study is to investigate a novel toughening approach for liquid mouldable carbon fibre/epoxy composites. The toughening mechanism is based on the use of thermoplastics for the toughening of epoxy resins in which polymer blends are formed, leading to phase separated morphologies which allows for various toughening mechanisms to take place. Instead of standard melt or solution blending, the thermoplastic in this study is introduced as solid phenoxy fibres, which are combined with dry carbon fabric preforms. These phenoxy fibres remain solid during resin infusion and dissolve when the laminates are heated and phase separation takes place before curing completed. The main benefits of this approach are that the viscosity of matrix resin remains low, which makes liquid moulding of these laminates possible. Localised and selective toughening of particular regions within a structure can also be achieved. Process time and cost can also be reduced by eliminating the polymer blending process. It was found that modification with phenoxy improved composite Mode-I interlaminar toughness significantly, with an increase of up to 10-folds for bifunctional epoxy composite and 100% for tetrafunctional epoxy composite, while tensile properties were not adversely affected. It was found that it is possible to combine the dissolvable phenoxy fibres with an undissolved aramid interleaf to improve toughness and damage properties. However, the phenoxy-epoxy systems had lowered environmental stability and degraded after hot-wet and solvent conditioning.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:667218 |
| Date | January 2013 |
| Creators | Wong, Doris Wai-Yin |
| Publisher | Queen Mary, University of London |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://qmro.qmul.ac.uk/xmlui/handle/123456789/8710 |
Page generated in 0.0017 seconds