Orientador: Andréia Bolzan de Paula / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T14:47:47Z (GMT). No. of bitstreams: 1
Ozera_EduardoHaruki_M.pdf: 1583076 bytes, checksum: 79af0fa55e9064c477b566a17965f419 (MD5)
Previous issue date: 2013 / Resumo: O objetivo neste estudo foi avaliar a influência da degradação promovida por bebidas ácidas no brilho e cor de materiais restauradores estéticos. Foram confeccionadas 40 amostras circulares para cada compósito: um nanoparticulado (Filtek Z350XT) e dois nanohíbridos (IPS Empress Direct e Charisma Diamond) com dimensões de 8 mm x 2 mm e armazenadas em estufa a 37ºC. Após 24 horas, foi realizado o polimento com discos abrasivos de óxido de alumínio Sof Lex Pop On (3M/ESPE) e realizadas as mensurações iniciais do brilho e cor de superfície. Em seguida, as amostras foram aleatoriamente separadas em 12 grupos (n=10) de acordo com o material restaurador e solução de degradação: saliva artificial (pH=7), suco Cranberry (pH=2,76), Coca-Cola (pH=2,54) e café (pH= 5). Cada amostra foi imersa em 4 mL de solução por 15 minutos, 3 vezes ao dia durante 14 dias. Após esse período, a cor foi mensurada por espectrofotometria de refletância e o brilho de superfície por meio de medidor de brilho. Foram calculados o ?E da cor e a variação de brilho (final - inicial) e os dados foram avaliados quanto à normalidade pelo teste de Kolmogorov-Smirnov, apresentando distribuição normal (p<0,05). Os dados foram submetidos à ANOVA 2 fatores e ao teste Tukey (5%). O ?E da cor para os compósitos Filtek Z350 e Charisma Diamond foi significativamente maior quando degradados em café e suco. Para a IPS Empress Direct o café promoveu maior alteração de cor seguido do suco, Coca-Cola e saliva, com diferença significativa. Quando analisada a influência de cada solução nos materiais, a Coca-Cola não influenciou na alteração de cor dos compósitos. O café promoveu menor alteração de cor no compósito Charisma Diamond. O suco e a saliva promoveram maior alteração de cor no Filtek Z350, quando comparado ao Charisma Diamond. O café e o suco promoveram maior perda de brilho no compósito Filtek Z350, enquanto que para IPS Empress Direct e Charisma Diamond maior perda de brilho foi promovida pelo café. Quando analisada a influência da solução nos diferentes materiais, observou-se que a Coca-Cola não influenciou na perda de brilho dos compósitos, enquanto o café promoveu maior perda de brilho no compósito IPS Empress Direct. O suco Cranberry promoveu maior perda de brilho no Filtek Z350, quando comparado aos compósitos IPS Empress Direct e Charisma Diamond, os quais foram similares. A saliva promoveu maior perda de brilho no Charisma Diamond quando comparado ao IPS Empress Direct. As bebidas ácidas utilizadas neste estudo influenciaram negativamente as propriedades ópticas de brilho e cor de materiais restauradores, sendo estas, material dependente / Abstract: The aim of this study was to evaluate the influence of different solutions promoted by degradation on gloss and color of esthetic restorative materials. Forty samples were prepared for each composite: a nanofilled (Filtek Z350XT) and two nanohybrid (IPS Empress Direct and Charisma Diamond) with dimensions of 8 mm x 2 mm and stored at 37 º C. After 24 hours, the polishing was conducted with the system Sof Lex Pop On(3M/ESPE) and performed initial gloss and color measurements. Then, the samples were randomly divided into 12 groups (n = 10) in accordance with the restorative material and degradation solution: artificial saliva, Cranberry juice, Coca-Cola and coffee. Each sample was immersed in 4 mL of solution per 15 minutes, three times a day for 14 days. After this period, the color and gloss of the surface were measured again. Were calculated the color ?E and gloss variation (final - initial) and the data was evaluated for normality using the Kolmogorov-Smirnov test presenting normal distribution (p< 0.05). The data were submitted to 2 factors ANOVA and Tukey's test (5%). The Filtek Z350 and Charisma Diamond ?E was significantly higher when degraded in coffee and juice. For IPS Empress Direct, coffee promoted greater color change followed by juice, Coca-Cola and saliva, with a significant difference. When analyzing the influence of each solution in the materials, Coca-Cola did not influence the color change of the composites. The coffee promoted less color change in the composite Charisma Diamond. The juice and saliva promoted greater color change in Filtek Z350 compared to Charisma Diamond. Coffee and cranberry juice promoted higher brightness loss in Filtek Z350, while the IPS Empress Direct Diamond Charisma and greater loss of gloss was promoted by the coffee. When analyzing the influence of different materials in solution, it was observed that Coca-Cola did not influence the loss of gloss of composites, while the coffee promoted greater brightness loss in the composite IPS Empress Direct. Cranberry juice caused greater loss of brightness in Filtek Z350, compared to composite IPS Empress Direct and Charisma Diamond, which were similar. Saliva promoted greater loss of gloss on Charisma Diamond when compared to IPS Empress Direct. The beverages used in this study influenced the otical surface properties of the composites studied / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288578 |
| Date | 04 April 2013 |
| Creators | Ozera, Eduardo Haruki, 1988- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Paula, Andreia Bolzan de, Consani, Simonides, Alonso, Roberta Caroline Bruschi |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 63 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds