In this work, the magnetoimpedance (MI) and magnetization dynamics in multilayered
Ni81Fe19/Ag and Ni81Fe19/Cu samples are studied. The samples were produced by magnetron
sputtering at the Laboratório de Magnetistmo e Materiais Magnéticos da UFSM with
Py=Ni81Fe19 thickness of 100Å and 200Å, while the Ag layers were grown with 7Å, 14Å,
25Å, 50Å, 100Å and 200Å in the case of Py/Ag samples. For the Py/Cu samples, the Py layer
was kept constant at 100Å, while the Cu layer was kept with 25Å. The 15, 30, 50, 70 and 100
number of bilayers was kept in all set of samples. The magnetoimpedance measurements were
performed in the frequency range 100kHz 1.8GHz. MI ratios of 240% were observed in the
[Py(100Å)/Ag(25Å)]x100 system, while 253% was obtained in the [Py(100Å)/Cu(25Å)]x100
system at 1.8GHz and 709MHz, respectively. In the case of the Py/Ag samples, a multiple
peak structure (4 to 6 peaks) was observed whenever the Py/Ag thickness ratio was 4. These
multiple peak structures are possibly associated to multiple ferromagnetic resonance
frequencies in these particular samples. The experimental relations of dispersion were
obtained for all samples that presented FMR in the studied frequency range. The results are
discussed in terms of the induced magnetic anisotropies associated to the sputtering guns and
also taking into account the more important interactions between the magnetic layers. / Nesse trabalho foram estudados o efeito magnetoimpedância (MI) e a dinâmica da
magnetização em multicamadas de Ni81Fe19/Ag e Ni81Fe19/Cu. As amostras foram produzidas
usando a técnica de magnetron sputtering no Laboratório de Magnetismo e Materiais
Magnéticos da UFSM com as espessuras de 100 e 200Å para as camadas de Py=Ni81Fe19 e
com as espessuras de 7, 14, 25, 50, 100 e 200Å para as camadas de Ag, no caso das amostras
de Py/Ag. Para as amostras de Py/Cu, a espessura da camada de Py foi mantida constante em
100Å, enquanto as camadas de Cu foram mantidas com 25Å de espessura. O número de
bicamadas foi de 15, 30, 50, 70 e 100 em quase todo o conjunto de amostras. As medidas de
MI foram feitas na faixa de freqüências de 100kHz 1.8GHz. Foram observadas razões de
magnetoimpedância com valores de 240% no caso do sistema [Py(100Å)/Ag(25Å)]x100 e de
253% no sistema [Py(100Å)/Cu(25Å)]x100 nas freqüências de 1.8GHz e 709MHz,
respectivamente. No caso das amostras de Py/Ag, foi observada uma estrutura de picos
múltiplos sempre que a razão entre as espessuras de Py e de Ag assumia o valor 4. As
estruturas de picos quádruplos e sêxtuplos possivelmente estão associadas a múltiplas
ressonâncias ferromagnéticas nessas amostras. Foram obtidas as relações de dispersão
experimentais para as amostras que apresentaram ressonância ferromagnética na faixa de
freqüências estudada. Os resultados são discutidos em termos das anisotropias induzidas nas
amostras pelos canhões de sputtering e em termos das interações mais relevantes entre as
camadas magnéticas.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsm.br:1/3923 |
| Date | 29 May 2006 |
| Creators | Andrade, Antonio Marcos Helgueira de |
| Contributors | Sommer, Rubem Luis, Lima, Luiz Carlos Sampaio, Schmidt, Joao Edgar, Silva, Celso Arami Marques da, Magalhães, Sergio Garcia |
| Publisher | Universidade Federal de Santa Maria, Programa de Pós-Graduação em Física, UFSM, BR, Física |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFSM, instname:Universidade Federal de Santa Maria, instacron:UFSM |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 100500000006, 600, 300, 300, 300, 300, 300, 300, 39531fe3-45a0-4cd6-9ece-939f0329ddbb, 785e4235-5b50-4a71-aa26-e4dfa85ca81f, 65d49c9b-acc5-432e-8f35-685041c95f45, f01d81cc-fa54-4a4f-96a1-827c7cb675b3, d7226b02-56e4-4982-8c8d-1bcb92abbb6d, 57b4a084-24b8-4597-b681-d1fb3fc94c77 |
Page generated in 0.0027 seconds