Previous issue date: 2009-12-17 / Capes / A expansão por umidade (EPU) consiste na expansão sofrida por alguns materiais cerâmicos quando em contato com água na forma líquida ou de vapor. O processo de EPU quando desenvolvido em blocos cerâmicos pode acarretar o aparecimento de trincas em alvenarias ou mesmo danos estruturais mais severos. Nos últimos anos, os estudos desenvolvidos sobre EPU e resistência mecânica, estão centrados em materiais para revestimentos cerâmicos, com poucos dados relativos ao comportamento mecânico de blocos cerâmicos sujeitos à EPU. Neste contexto, este trabalho objetiva estudar a influência do teor de quartzo na EPU e no comportamento mecânico de massas cerâmicas para uso em blocos furados. Para tanto, foram analisadas amostras de massas usadas na fabricação de blocos cerâmicos, oriundas de Parelhas-RN. À argila plástica foi adicionado quartzo nos teores de 10, 20 e 30%. Os corpos de prova, moldados por extrusão, queimados nas temperaturas de 850, 900 e 950º C, foram submetidos ao ensaio de aceleração de EPU por autoclavagem com pressão de 0,7 MPa por 5 h e resistência mecânica à flexão com carregamento em três pontos. A EPU foi determinada por dilatometria a 600oC. Os resultados indicam que a adição de quartzo finamente moído, nos teores especificados e nas condições estudadas, de uma forma geral, pouco influenciou nos resultados de EPU, exceto para a adição de 30%, e que a adição de quartzo fino em proporções mais elevadas reduz o comportamento mecânico dos blocos cerâmicos. / The Moisture Expansion (EPU) is the expansion experienced by some ceramic materials when in contact with water in liquid or vapor. The process developed EPU when bricks can cause the appearance of cracks in masonry or even more severe structural damage. In recent years, studies done on EPU and mechanical strength, focus on materials for ceramic tiles, with few data on the mechanical behavior of ceramic blocks subject to the EPU. In this context, this work aims at studying the influence of quartz content in the EPU and the mechanical behavior of ceramic bodies for use in blocks bored. To that end, samples were analyzed mass used in the manufacture of ceramic bricks, coming from Parelhas-RN. In plastic clay was added in the quartz contents of 10, 20 and 30%. The samples, cast extrusion, burned at temperatures of 850, 900 and 950 ° C, were tested on accelerating EPU by autoclaving at a pressure of 0.7 MPa for 5 h and flexural loading with three points. The EPU was determined by dilatometry to 600 °C. The results indicate that the addition of finely ground quartz, the levels specified under the conditions studied, in general, had little influence on the results of public schools and that the addition of fine quartz in higher rates reduces the mechanical behavior of ceramic blocks.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1707 |
Date | 13 September 2018 |
Creators | MEDEIROS, Rosinaldo do Rio. |
Contributors | FERREIRA, Heber Carlos., NEVES, Gelmires de Araújo., SANTANA, Lisiane Navarro de lima., FERREIRA, Heber Sivini., MENEZES , Romualdo Rodrigues., CAMPOS, Liszandra Fernanda Araújo. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds