The diploma thesis is focused on fire-resistant repair mortar with fine-grained filler. The aim of this work is the research and development of fine-grained Mortars resistant to high temperatures, which are characteristic at the beginning of the fire. The theoretical knowledge with subsequently realized laboratory verification was used. At-tention was paid to the masses based on the mixed binder comprising cement and blast furnace slag, respectively. high-temperature ash. Cellulose fibres were used as the dis-persed reinforcement. Two kinds of aggregate were assessed - fly ash agloporit and am-phibolite incl. combinations thereof. Laboratory tests were carried out via determination of basic material properties (density, strength, consistency, dimensional changes etc.) after exposure to extreme temperatures. A substantial part of the research was also study of different cooling conditions - slow and fast (water and air). Selected formulations were subjected to temperatures up to 1200 ° C. In the conclusion is selected several recipes that have been found to be optimal for continuing research on the basis of the results and findings.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:227280 |
| Date | January 2015 |
| Creators | Záruba, Jiří |
| Contributors | Gross,, Tomáš, Bydžovský, Jiří |
| Publisher | Vysoké učení technické v Brně. Fakulta stavební |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds