Overload effects on the fatigue crack propagation behaviour in Inconel 718

In this master thesis, work done in the TURBO POWER project High temperature fatigue crack propagation in nickel-based superalloys during spring 2012 will be presented. The overall objective of this project is to develop and evaluate tools for designing against fatigue in gas turbine applications, with special focus on the crack propagation in the nickel-based superalloy Inconel 718. Experiments have been performed to study the effect of initial overloads, and it has been shown that even for small initial overloads a significant reduction of the crack growth rate is received. Furthermore, FE simulations have been carried out in order to describe the local stress state in front of the crack tip since it is believed to control, at least partly the diffusion of oxygen into the crack tip and thus also the hold time crack growth behaviour of the material. Finally, an evaluation method for the stresses is presented, where the results are averaged over an identifiable process/damaged zone in front of the crack tip.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:liu-77494
Date January 2012
CreatorsLundström, Erik
PublisherLinköpings universitet, Hållfasthetslära, Linköpings universitet, Tekniska högskolan
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0018 seconds