Title: Optical and magneto-optical studies of ferrimagnetic garnets for photonic and spintronic applications Author: RNDr. Lukáš Beran Department: Intitute of Physics of Charles University Supervisor: RNDr. Martin Veis, PhD., Institute of Physics of Charles University Abstract: This doctoral thesis is devoted to fabrication and systematic char- acterization of physical properties of thin films of iron garnets with potential applications in photonic and spintronic devices. Investigated samples were pre- pared by metallo-organic decomposition and pulsed laser deposition. The study was focused on structural and magnetic characterizaiton along with optical and magneto-optical properties. Obtained experimental results were further con- fronted with theoretical calculations. The application potencial of garnets for photonic devices was discussed based on determined Figure of Merit (Faraday rotation to optical loss ratio). High values were achieved for single crystal thin film of Ce doped yttrium iron garnet on galium gadolinium garnet substrate as well as for pollycrystalline Bi doped yttrium iron garned on silicon substrate. Furthermore, new rare-earth garnets were prepared with attempt to achieve per- pendicular magnetic anisotropy of these film. This was achieved for three di erent materials, which were not...
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:436352 |
| Date | January 2020 |
| Creators | Beran, Lukáš |
| Contributors | Veis, Martin, Dubroka, Adam, Výborný, Karel |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds