While using iron castings behind temperature of 500 C namely at cyclic heat straining degradation of structure and breaching iron castings. For this purpose introduce cast iron with content of Si and Mo. Focusing on improvement of SiMo51 for increased high-temmperature corrosion-and fatigue life in exhaust-gas temperatures up to 800 C. Thesis set up chemical microheterogeneity, properties, high temperature corosion and microhardness