Orientador: Chang Tien Kiang / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-23T10:58:17Z (GMT). No. of bitstreams: 1
GildelosSantos_Diego_M.pdf: 3846338 bytes, checksum: 236d6bd77c86a1c77d95cb220ea5b5d3 (MD5)
Previous issue date: 1998 / Resumo: O presente trabalho mostra os estudos realizados sobre o processamento das blendas de poli(tereftalato de etileno) (PET) e do polipropileno (PP) numa escala semi-industrial. Analisou-se a influência da presença do polipropileno enxertado com anidrido maleico (PP-g-MA) como agente compatibilizante, sendo adicionado numa proporção de 3 % em peso sobre o peso total da mistura. As blendas dos materiais com e sem compatibilizante foram estudadas nas relações de PET/PP 75/25, 50/50 e 25/75, respectivamente. Inicialmente os materiais foram homogeneizados numa dupla rosca semi industrial ZSK 30 W 9/2 sendo posteriormente reprocessados numa instalação piloto de fiação da Plasticisers para a obtenção dos fios. As diferentes blendas e fios produzidos com elas foram analisados através de ensaios térmicos, mecânicos e morfológicos. Através da caracterização térmica obteve-se informações da cinética de cristalização permitindo a confirmação das avaliações anteriormente realizadas no Departamento de Tecnologia de Polímeros da Faculdade de Engenharia Química da UNICAMP com relação à aceleração do processo de cristalização dos materiais, estando um na presença do outro. Os ensaios térmico e mecânico demonstraram que o compatibilizante provocou a diminuição das tensões interfaciais. O aumento na orientação dos fios e as tensões suportadas por estes, associado à melhoria das condições de processamento mostraram a vantagem do uso do compatibilizante. As análises de microscopia eletrônica de varredura permitiram notar a influência da composição da mistura e da presença do compatibilizante na estabilização das estruturas morfológicas das blendas quando do seu reprocessamento para a obtenção dos fios. As morfologias das blendas obtidas na dupla rosca foram comparadas com as apresentadas nas amostras dos mesmos materiais produzidas num equipamento de bancada (Minimax Molder CS 183 - MMX). Comprovaram-se limitações do Minimax na simulação do comportamento dos materiais quando realiza-se uma ampliação na escala de processamento. Os ensaios de tingimento realizados nos fios das blendas constataram a possibilidade de uso do processo de tingimento em solução para as blendas estudadas / Abstract: The results of the study on the processinn in semi-industrial scale of blends with varying compositions of polyethylene terephthalate (PET) and polypropylene (PP) are reported in this work. The influence of polypropylene grafted with maleic anhydride (PP-g-MA) present at 3 % in the mixture was studied. Blends of PET/PP at proportions of 75/25, 50/50 e 25/75, respectively, with and without compatibilizer were studied. The materiais were initially homogenized in a semi-industrial twin screw ZSK 30 W 9/2 and then processed in a Plasticisers pilot spinning equipment to obtain the yarns. Thermal, mechanical and morphological characterizations performed with the mixtures and the spun yarns. Thermal characterization gave information on the kinetics of crystallization, confirming data of assays previously done at the Departarl1ento de Tecnologia de Polímeros of the Universidade Estadual de Campinas, Brazíl, as regard to the acceleration of the crystallization when both materiais are processed together. Thermal and mechanical assays showed that the compatibilizer decreased interfacial tensions. On the otherhand, compatibilizers increased the orientation of the yarns and the tensions they supported. Microscopy showed the influence of mixture composition on the stabilization of the morphological structures of the blends when they are used to produce yarns. These morphologies were also compared to those of previous studies obtained in a bench scale mixer (Minimax Molder CS183-MMX). The yarns produced from the blends of this study could be solution-dyed, which is of major technological interest / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266358 |
| Date | 27 February 1998 |
| Creators | Gil de los Santos, Diego |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Chang, Tien-Kiang, 1957-, Kiang, Chang Tien, 1957-, Dias, Marcos Lopes, Peres, Leila |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 84f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0468 seconds