This study focused on the comparison of the electrospun silk scaffolds to the electrospun silk fibroin gel scaffolds. Moreover, this study examined the differences in cross-linking effects of genipin and methanol as well as solvents on the mechanical properties and cell compatibility of the scaffolds. Silk scaffolds were electrospun from an aqueous solution or 1,1,1,3,3-hexafluoro-2-propanol (HFIP) without genipin, immediately after 8 % (wt) genipin was added to the solution, and 18 hours after genipin blended with the solution. Uniaxial tensile testing determined that the silk scaffolds electrospun from water exhibit a higher modulus and peak stress than that of the silk scaffolds electrospun from HFIP. In vitro cell culture was conducted to determine the cell compatibility of the various silk fibroin-based scaffolds. 4'-6-Diamidino-2-phenylindole (DAPI) staining and histology suggest that genipin may enhance cell compatibility, and that neither ethanol nor methanol inhibit cell interactions.
| Identifer | oai:union.ndltd.org:vcu.edu/oai:scholarscompass.vcu.edu:etd-3527 |
| Date | 27 July 2011 |
| Creators | McCool, Jennifer |
| Publisher | VCU Scholars Compass |
| Source Sets | Virginia Commonwealth University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
| Rights | © The Author |
Page generated in 0.0017 seconds