Two magnesium alloys (Mg-4Y-4Gd-2Ca and Mg-2Y-2Gd-1Ca) with high ignition tem- perature were successfully processed by extrusion. Mg-2Y-2Gd-1Ca alloy was addition- ally processed by equal channel angular pressing (ECAP) to achieve ultrafine-grained microstructure. The effect of extrusion parameters on fraction of recrystallized grains, grain size, and texture was revealed by EBSD analysis. The presence of Mg2Ca, REH2 and Mg5RE secondary phases was proven by SEM and TEM. Microstructural condition including distribution and morphology of secondary phase par- ticles directly affected the mechanical properties. Yield tensile stress exceeding 200 MPa was achieved in each condition. Large non-recrystallized grains with strong {10̄10} tex- ture resulted in a significant anisotropy in mechanical properties. Processing by ECAP led to a homogeneous microstructure with a mean grain size below 1 µm. ECAP condition showed superior mechanical properties with a low anisotropy. The developed and analysed microstructural condition resulted in favourable mechanical properties. The studied alloys are therefore promising for the application in aerospace industry. 1
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:448480 |
| Date | January 2021 |
| Creators | Šašek, Stanislav |
| Contributors | Stráská, Jitka, Hadzima, Branislav |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0022 seconds