As the environmental concern grows, researchers try to find material which can be environmental friendly and biodegradable to some extent. At present, flax fibre cannot fully replace glass fibre. Some attempts have been made to replace the glass fibre.<p>
Studies show the physical and mechanical properties of natural fibres are comparable with glass fibre, so it can replace glass fibre in the process of making biocomposites. <p>
The properties of biocomposites depend on the fibre used. Research shows that to get a better biocomposite, the fibre has to be chemically treated to improve adhesion between fibre and polymer matrix. After the chemical treatment, the fibre has to be dried to minimum moisture content so the drying of flax fibre is essential in the process of making biocomposites. <p>
In this research, oilseed flax fibre is dried and drying characteristics were investigated. After drying, the physical properties of the fibre were tested and analysed.<p>
The fibre was dried using three different drying methods, namely, microwave, microwave-convection, and microwave-vacuum environments. Curve fitting with four empirical methods has been carried out to determine the drying constant, coefficient of determination and standard error values.
The results showed that microwave-vacuum drying method is more efficient (in terms of final moisture content) than microwave and microwave-convection drying. Although microwave-vacuum drying took the most time and did not result in promising colour values, the maximum moisture removal is achieved because fibres can be dried for a longer period of time with a comparatively low temperature.<p>
The results of physical properties were analysed for untreated and treated and dried flax fibre. The tensile strength and elastic modulus of untreated and treated fibre did not show any significant change. Because the diameter of flax fibre cannot be consistent, a range of values can be obtained. The diameter range of fibre bundle 30-300 µm was examined for these tests. The tensile strength obtained from these fibre bundles ranged between 16 to 667 MPa and elastic modulus values were 2 GPa up to 63 GPa.<p>
The scanning electron micrograph (SEM) was also analysed for untreated and treated-dried fibre. The fibre which was dried with high power or longer period of time showed black spots, probably due to local heating. The fibre dried with microwave-vacuum developed some black spots which were clearly seen in the SEM.<p>
Differential scanning calorimetric data showed a shift in temperature of degradation. In this research, degradation temperature of cellulose was found 350(+/-10)°C for the treated and dried flax fibre.<p>
In conclusion, the flax fibre has a potential to be used in biocomposite production. The microwave-vacuum works best for drying where the fibre can be dried up to a less than 1% of moisture content.
| Identifer | oai:union.ndltd.org:USASK/oai:usask.ca:etd-04172009-121327 |
| Date | 20 April 2009 |
| Creators | Tripathy, Ananda Chandra |
| Contributors | Meda, Venkatesh, Panigrahi, Satyanarayan, Tabil, Lope G., Maule, Charles P., Soltan, Jafar |
| Publisher | University of Saskatchewan |
| Source Sets | University of Saskatchewan Library |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://library.usask.ca/theses/available/etd-04172009-121327/ |
| Rights | unrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report. |
Page generated in 0.0021 seconds