The Vanadium bromide (V/Br) flow cell employs the Br3-/Br- couple in the positive and the V(II)/V(III) couple in the negative half cell. One major issue of this flow cell is bromine gas formation in the positive half cell during charging which results from the low solubility of bromine in aqueous solutions. Bromine complexing agents previously used in the zinc-bromine fuel cell were evaluated for their applicability in V/Br flow cell electrolytes. Three quaternary ammonium bromides: N-ethyl-N-methyl-morpholinium bromide (MEM), N-ethyl-N-methyl-pyrrolidinium bromide (MEP) and Tetra-butyl ammonium bromide (TBA) were studied. It is known that aqueous bromine reacts with quaternary ammonium bromides to form an immiscible organic phase. Depending on the number of quaternary ammonium bromides used and the environmental temperature, the second phase formed will either be solid or liquid. As any solid formation would interrupt the flow cell operation, potential formation of such kind has to be eliminated. Stability tests of simulated V/Br electrolyte with added quaternary ammonium bromides were carried out at 11, 25 and 40 oC. In the absence of bromine, the addition of MEM, MEP and TBA were found to be stable in V/Br electrolytes. However, in the presence of bromine, solid formation was observed in the bromine rich organic phase when the V/Br electrolyte contained a single quaternary ammonium bromide (QBr) compound. For V/Br electrolytes with binary or ternary QBr mixtures containing TBA, the presence of bromine caused a viscous polybromide phase to form at room temperature and the release of bromine gas at higher temperature. Only a binary mixture of MEM and MEP formed a stable liquid organic phase between 11 ?? 40 oC. In this study it was found that V/Br electrolytes containing a binary QBr mixture (0.75M) of MEM and MEP gave the best combination that formed an orange oily layer in the presence of bromine without solidification between 11 ?? 40oC. Furthermore, it was found that samples of V/Br electrolytes containing a ternary QBr mixture, are less effective in bromine capturing if the total QBr concentration was less than 1 M at 40oC, where bromine gas evolution was observed. From electrochemical studies of V3+/V2+, it was found that the addition of MEM and MEP had a minimal effect on the formal potential of the V3+/V2+ couple, the V2+/V3+ transfer coefficient and the diffusion coefficient of V3+. Therefore, MEM and MEP can be added to the negative half-cell of a V/Br flow cell without major interference From linear sweep voltammetry, the kinetics of the Br-/Br3- redox couple was found to be mass transfer controlled. After the addition of MEM and MEP mixture, the exchange current density was found to decrease from 0.013 Acm-2 to 0.01 Acm-2. On the other hand the transfer coefficient before and after MEM and MEP addition was found to be 0.5 and 0.44 respectively. Since the kinetic parameters were not significantly affected by the addition of MEM and MEP mixture, they can be added to the positive half-cell of the V/Br flow cell as bromine complexing agents. The electrochemical studies of both V3+/V2+ and Br-/Br3- showed the addition of MEM and MEP has minimal interference with the redox reactions of the vanadium bromide flow cell. This thesis also investigated the effect of MEM and MEP addition on the cell performance of a lab scale V/Br flow cell using two different membranes (ChiNaf and VF11). Flow cell performance for 2 M V3.7+ + 0.19 M MEM + 0.56 M MEP electrolytes utilising ChiNaf membrane at 10 mAcm-2 produced an energy efficiency of 59%, and this decreased to 43% after 15 cycles. For the static cell utilising VF11 membrane, the addition of MEM and MEP reduced the energy efficiency from 59.7% to 43.4%. It is believed that this is caused by the mass transfer controlled Br-/Br3- couple in the complexed positive half-cell solution. Therefore, uniformity between the organic and aqueous phase is important for flow cells utilising electrolytes with MEM and MEP. Finally, the polarization resistance of a lab scale V/Br flow cell utilising ChiNaf membrane and 2 M V3.7+ electrolytes was found to be slightly higher during cell charging (3.9 cm2) than during the discharge process (3.6 cm2), which is opposed to that in the all-vanadium redox cell.
| Identifer | oai:union.ndltd.org:ADTP/215707 |
| Date | January 2008 |
| Creators | Poon, Grace, Chemical Sciences & Engineering, Faculty of Engineering, UNSW |
| Publisher | Publisher:University of New South Wales. Chemical Sciences & Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://unsworks.unsw.edu.au/copyright, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0017 seconds