Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2013 / Made available in DSpace on 2014-08-06T17:51:47Z (GMT). No. of bitstreams: 1
321959.pdf: 43208066 bytes, checksum: cc29e28d59a330043fbbac9ec59764a1 (MD5)
Previous issue date: 2013 / A argamassa autonivelante é um material de baixa viscosidade
constituído por aglomerante, areia, água e aditivos. Sua principal
característica é a elevada fluidez, visto que apresenta grande habilidade
de espalhamento e nivelamento. Existem dois tipos de argamassas
autonivelantes: à base de sulfato de cálcio (normalmente anidrita) e à
base de cimento (Portland ou Sulfoaluminoso). Àquelas de sulfato de
cálcio possuem rápido endurecimento, sem retração acentuada e pouca
fissuração, contudo, podem ser sensíveis à umidade. Uma maneira de
melhorar essa característica se dá mediante a utilização do cimento
aluminoso. O uso deste tipo de cimento, que é rico em alumina, ocorre
normalmente em sistemas ternários de cimento aluminoso, sulfato de
cálcio e cimento Portland. Esses sistemas ternários são designados
etringíticos e esta denominação está relacionada ao principal produto
hidratado que é a etringita (C3A.3CS.H32). O fosfogesso, ou gesso
químico, pode ser uma fonte de sulfato de cálcio para as argamassas
autonivelantes. Pode-se obter a forma de sulfato de cálcio denominada
anidrita a partir de seu tratamento térmico. Deste modo, com base na
calcinação do fosfogesso nas temperaturas de 350°, 450°, 550° e 650°
foi produzida uma anidrita sintética, chamada de fosfoanidrita (FGA).
FGA, fosfogesso seco (FG REF) e Hemidrato Beta foram os tipos de
sulfatos de cálcio utilizados para a produção de argamassas
autonivelantes em sistemas ternários e binários. Os sulfatos de cálcio
foram caracterizados por granulometria a laser, ATD/TG, DRX, MEV,
solubilização e solubilidade. A caracterização permitiu detectar a
obtenção da anidrita II, que é uma forma pouco solúvel. As argamassas
autonivelantes foram avaliadas quanto à resistência mecânica,
espalhamento e sua manutenção, tempo de escoamento mediante o funil-
V, tempo de pega, calorimetria e degradação em água por ciclos de
imersão e imersão-secagem. Por meio do estudo dos cristais formados e
sua morfologia, por DRX e MEV, identificou-se a influência do tipo de
sulfato de cálcio usado e também do sistema aglomerante em
propriedades de absorção de água por capilaridade, isotermas de
adsorção, estabilidade dimensional e compatibilidade ambiental. Os
resultados mostraram que, tanto o período quanto a temperatura de
calcinação do fosfogesso, são fundamentais para o melhor desempenho
de argamassas autonivelantes, entretanto, o sistema de aglomerantes
mostrou-se, igualmente, ser um fator determinante. Conseguiu-se
produzir um sistema etringítico a partir do uso de FGA em argamassas
autonivelantes e constatou-se que estas argamassas, quando elaboradas
com FGA calcinada por período de 4 horas em temperatura superior a
450°C, são resistentes da degradação em água. A morfologia da etringita
é extremamente influente na estabilidade dimensional dos materiais,
pois se detectou a etringita massiva que causa fissuração e expansão no
estado endurecido <br> / The self-leveling underlayment is a material of low viscosity consisting
of binder, sand, water and additives. Its main feature is the high fluidity,
since it has great ability to spread and level itself. There are two types of
self-leveling underlayments: based on calcium sulfate (anhydrite
usually) and based on cement (Portland or Sulfoaluminate). Those of
calcium sulfate have rapid hardening, without pronounced shrinkage and
little cracking, however, may be sensitive to moisture. For improving
this characteristic the calcium aluminate cement is typically used. The
use of this type of cement, which is rich in alumina, normally occurs in
ternary systems of calcium aluminate cement, calcium sulfate and
Portland cement. These blends are called ettringite systems and this
name is related to the main hydrated product which is the ettringite
(C3A.3CS.H32). The phosphogypsum or chemical gypsum, can be a
source of calcium sulfate for the production of self-leveling
underlayments. The anhydrite can be obtained from heat treatment.
Thus, based on phosphogypsum calcining at temperatures of 350°, 450°,
550° and 650° it was produced a synthetic anhydrite, called
phosphoanhydrite (FGA). FGA, phosphogypsum dried (FG REF) and
beta hemihydrate were the types of calcium sulphates used for the
production of self-leveling underlayments in binary and ternary systems.
The calcium sulphates were characterized by laser granulometry,
DTA/TG, XRD, SEM, solubility and solubilization. The
characterization made possible to detect the obtention of the anhydrite
II, which is a slightly soluble form. The self-leveling underlayments
were evaluated for mechanical strength, consistency and its
maintenance, flow time with the funnel-V, setting time, calorimetry and
degradation in water by cycles of immersion and immersion-drying.
Through the study of crystals formed and their morphology, by XRD
and SEM, it was found the influence of the type of calcium sulfate used
and also of the binder system in properties like water absorption by
capillary, adsorption isotherms, dimensional stability and compatibility
environment. The results showed that both the period and the calcination
temperature of phosphogypsum are key to the improved performance of
self-leveling underlayments, however, the binder system proved to be a
determinative factor as well. It was possible to produce an ettringite
system from the use of FGA in self-leveling underlayments and it was
found that these mortars prepared with FGA when calcined for 4 hours
at temperature above 450°C are resistant to water degradation. The
morphology of ettringite is extremely influential in the dimensional
stability of materials because the massive ettringite that causes
expansion and cracking in the hardened state was detected.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/123140 |
Date | January 2013 |
Creators | Schaefer, Cecília Ogliari |
Contributors | Universidade Federal de Santa Catarina, Rocha, Janaíde Cavalcante |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 387 p.| il., tabs., grafs. |
Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds