Avaliação clínica, histológica e histomorfométrica do reparo de defeitos ósseos criados em mandíbula de cães preenchidos com Biovidro 45S5 ou Biosilicato® após a colocação de implantes osseointegráveis / Bone formation on Ti implants in intra-bony defect sites filled with different bone substitutes: histomorphometric analysis in dogs

O presente trabalho avaliou a formacao de tecido osseo ao redor de implantes osseointegraveis de titanio, apos realizacao de defeitos osseos, utilizando diferentes tipos de substitutos osseos. Foram utilizados 5 caes de raca indeterminada, os pre molares e molares mandibulares foram extraidos, passados 12 semanas, os caes foram submetidos a um novo procedimento cirurgico aonde foram realizadas as perfurações preconizados pelo fabricante dos implantes, o osso vestibular da mandibula foi desgastado ate que parte da perfuracao fosse exposta, os implantes entao foram colocados nas respectivas perfuracoes, ficando com 4 espiras expostas. Esses defeitos foram preenchidos aleatoriamente com Bioglass® 45S5, Biosilicato® , Osso autogeno, e sem nenhum material de preenchimento. 18 semanas depois da colocacao dos implantes os caes foram mortos e suas hemi-mandibulas contendo os implantes removidas e submetidas aos analises histologiaos e histomorfometricas, os dados obtidos foram submetidos ao teste de Kruskal-Wallis. A histologia dos 4 grupos estudados revelaram a presenca de tecido osseo maduro em contato com os implantes, porem sem ralacao direta com os vidros bioativos e osso autogeno. A porcentagem de contato osso implante, matriz ossea mineralizada ao redor da espira, e area de espelho, nao mostraram diferencas estatisticas significantes entre os 4 materiais testados. Os resultados indicam que a presenca de substitutos osseos nao interfere com a formacao ossea ao redor dos implantes nesse modelo experimental. E existe resposta tecidual muito semelhante entre o osso autogeno, Bioglass® 45S5 e Biosilicato. / The aim of the present study was to investigate the amount of bone formation on Ti implants in sites with intra-bony defects filled with different bone substitutes. Mandibular premolars and first molars were extracted from 5 dogs, and after 12 weeks 3 implants were bilaterally placed in sites with intra-bony defects and each implantation site randomly received the following treatment: Biosilicate®, Bioglass® 45S5, aoutologous bone or no treatment. At 18 weeks after implantation, the hemi-mandibles containing the implants were removed and processed for morphological and histomorphometric analysis. Data were submitted to Kruskal-Wallis and Fishers test. The histological sections of the 4 experimental groups exhibited mature bone tissue in contact with implants, but not related with bioactive glasses or autologous bone used. The percentage of bone-implant contact, mineralized bone matrix between implant threads, and mineralized bone matrix within mirror area in the treated or non-treated sites were not statistically different among the 4 experimental groups. These results indicates that the presence of the bone substitutes evaluated here did not interfere with bone formation on Ti implants in sites with intra-bony defects. In addition, tissue response to Biosilicate® was similar to that of Bioglass® 45S5 and autologous bone.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-23012009-170150
Date31 October 2008
CreatorsJabur, Roberto de Oliveira
ContributorsBarros, Valdemar Mallet da Rocha
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0015 seconds