Estabilização de um solo fino laterítico pelo ácido fosfórico

Submitted by Fatima Fonseca (fatima.fonseca@sibi.ufrj.br) on 2017-06-23T13:12:43Z
No. of bitstreams: 1
127156.pdf: 1982795 bytes, checksum: 61427189e4a147d4198c8d4f98f6726d (MD5) / Made available in DSpace on 2017-06-23T13:12:43Z (GMT). No. of bitstreams: 1
127156.pdf: 1982795 bytes, checksum: 61427189e4a147d4198c8d4f98f6726d (MD5)
Previous issue date: 1971-07 / Estuda, em laboratório, a adequação do ácido fosfórico à estabilização de um solo laterítico fino. O solo estudado foi uma "terra roxa legítima", oriunda da Cidade de Campinas, Estado de São Paulo. Este é um solo laterítico, proveniente da alteração de diabásio, contendo 20% de Fe2 O3 livre, tendo 100% passado na peneira número 20 (0,84 mm) e 74,1% na número 200 (0,076 mm). Utilizando-se o ensaio de compressão simples, principalmente, investigaram-se as variáveis seguintes: I- Percentagem de ácido fosfórico (em relação ao peso do solo seco); II- Quantidade de solução empregada na compactação; III- Tempo de cura; IV- Energia de compactação; V- Temperatura de cura. Além das investigações acima citadas, que constituem o objeto principal do trabalho, realizaram-se também dois pequenos estudos: a) determinação da resistência à tração pelo método da compressão diametral; b) determinação da resistência à compressão simples de corpos de prova de solo tratado pelo cimento Portland, para comparação com um aditivo estabilizador comum. Os resultados mostram que o solo em questão, que era inadequado para uso como camada de um pavimento, após o tratamento com ácido fosfórico poderá vir a ter esta utilização. / A laboratory research work was performed in order do verify the possibilities of stabilizing a fine lateritic soil with phosphoric acid. A sample of "terra roxa legítima" from Campinas, São Paulo, was studied. This is a lateritic soil resulting from the weathering of a diabase, and presenting 20% of free Fe2 O3; it has 100% passing no. 20 sieve and 74.1% passing no. 200 sieve. The experimental work was carried out mainly through unconfined compression tests in order to observe the influence on strength of the following variables. I- Percentage of phosphoric acid (on a dry soil weight basis); II- Amount of solution used in compacting the soil; III- Curing time; IV- Compaction energy; V- Curing temperature. A few other secondary studies were also performed: a) tensile strength from diameter compression tests; b) unconfined compression tests of soil treated with Portland cement, to compare with a common stabilizing agent. According to the results obtained, the soil that was inadequate to be used in a pavement layer, became strong enough for that purpose when treated with phosphoric acid.

Identiferoai:union.ndltd.org:IBICT/oai:pantheon.ufrj.br:11422/2291
Date07 1900
CreatorsGuida, Hugo Nicodemo
Contributorshttp://lattes.cnpq.br/7642409540711794, Medina, Jacques de
PublisherUniversidade Federal do Rio de Janeiro, Programa de Pós-Graduação em Engenharia Civil, UFRJ, Brasil, Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa em Engenharia
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UFRJ, instname:Universidade Federal do Rio de Janeiro, instacron:UFRJ
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0018 seconds