Composite materials with laminated structure provide advantages which are utilised during component design. Low density, temperature and chemical stability are the profitable properties predetermining application of ceramic laminates. The main obstacle for wide spread of ceramic materials is their inherent brittleness. Therefore, in this thesis, the crack propagation in ceramics laminates has been extensively studied. Laminated structures with various volume fractions of components (alumina and zirconia) were prepared by electrophoretic deposition. Evaluation of crack propagation through the interface and determination of basic mechanical properties was conducted on the basis of extensive literature search. Crack deflection originated in both presence of internal stresses and differences in elastic modulus during the crack interface passing was monitored. A special type of specimen geometry was employed with the aim to set arbitrary angle between crack and interface. It was experimentally found that the degree of crack deflection is dependent on entering angle and volume fraction of components. Higher crack deflection was already found in the bulk of the test piece comparing to the test piece surface. The 3D fracture surface reconstruction generated using laser confocal microscopy was used in this detailed crack propagation study. Further basic elastic and strength characteristics of laminates were determined and compared to those obtained from monolithic materials. The validity of the mix rule for elastic characteristics was confirmed by comparing of elastics modulus. The most reliable method for elastic modulus determination was marked the dynamic resonance method due to low scatter and consistency in measurement. The flexural strength of all laminates tends to be close to the flexural strength of the weakest component. Therefore the mix rule is not applicable for flexural strength estimation on the contrary of elastic characteristics. The change of component volume fraction leads only to change of flexural strength scatter. Thanks to gained knowledge about crack propagation and basic characteristic determination will be possible to design ceramic laminates more efficiently for given needs of application.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:229300 |
| Date | January 2010 |
| Creators | Novotná, Lenka |
| Contributors | Trunec, Martin, Chlup, Zdeněk |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0016 seconds