Determinação de parâmetros para crescimento de trinca em ligas metálicas : modelagem e experimentação

Description

Dissertação (mestrado)— Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2010. / Submitted by Albânia Cézar de Melo ([e-mail]) on 2011-04-12T13:15:55Z
No. of bitstreams: 1
2010_JulioToshioMandai.pdf: 5833190 bytes, checksum: 62f633f30295d8edb7fbd85bf0f29a6a (MD5) / Approved for entry into archive by Daniel Ribeiro([e-mail]) on 2011-05-25T02:15:02Z (GMT) No. of bitstreams: 1
2010_JulioToshioMandai.pdf: 5833190 bytes, checksum: 62f633f30295d8edb7fbd85bf0f29a6a (MD5) / Made available in DSpace on 2011-05-25T02:15:02Z (GMT). No. of bitstreams: 1
2010_JulioToshioMandai.pdf: 5833190 bytes, checksum: 62f633f30295d8edb7fbd85bf0f29a6a (MD5) / O presente trabalho aborda um estudo numérico-experimental do comportamento de um
corpo de prova do tipo Compact Tension Specimen quando submetido a ensaios de
Tenacidade à Fratura (ASTM E399) e de Crescimento de Trinca por Fadiga (ASTM
E647). Como resultado deste trabalho foi gerado um código numérico, utilizando o software Ansys, como base no procedimento experimental desenvolvido a partir das normas
ASTM citadas acima, estabelecendo um padrão metodológico a ser aplicado na condução de testes de Mecânica da Fratura no Laboratório de Ensaios Mecânicos da UnB.
Adicionalmente, o desenvolvimento deste trabalho contribuiu para a melhor compreensão dos fenômenos de fratura em materiais metálicos, em especial do Aço
CA6NM e do Alumínio 7050 T7451, que foram os materiais utilizados nos ensaios
experimentais e na modelagem numérica. _________________________________________________________________________________ ABSTRACT / This work presents a numerical-experimental approach to analyze the behavior of a compact tension specimen when submitted to Fracture Mechanics Toughness Test (ASTM E399) and Fatigue Crack Growth Test (ASTM E647). As product of this work, a numerical code using Ansys software was developed to
simulate the experimental procedure, developed based on the ASTM standards
mentioned above. This procedure intends to provide a methodological basis to the tests
that will be carried out at Mechanical Research Laboratory of University of Brasilia
using compact tension specimen. Furthermore, along the development of this work, a better understanding of fracture phenomena in metallic materials was achieved, in special for CA6NM Steel and 7050 T7451 Aluminum, which were used in experimental tests and in numerical modeling.

Links & Downloads

1. MANDAI, Júlio Toshio. Determinação de parâmetros para crescimento de trinca em ligas metálicas: modelagem e experimentação. 2010. 162 f., il. Dissertação (Mestrado em Ciências Mecânicas)-Universidade de Brasília, Brasília, 2010.
2. http://repositorio.unb.br/handle/10482/8029

Tags

Mecânica de fratura

Metais

Modelagem numérica

Additional Fields

Identifer	oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/8029
Date	08 June 2010
Creators	Mandai, Júlio Toshio
Contributors	Ferreira, Jorge Luiz de Almeida
Source Sets	IBICT Brazilian ETDs
Language	Portuguese
Detected Language	Portuguese
Type	info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Source	reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB
Rights	info:eu-repo/semantics/openAccess