yes / In order to study the mechanical behaviors of engineered cementitious composites (ECC) reinforced with various types of polyvinyl alcohol (PVA) fibers and different fiber volume fractions after the freeze-thaw cycles, the rapid freeze-thaw method was used to test the mass loss ratios, longitudinal relative dynamic elastic modulus, compressive strength and flexural strength. The results showed that specimens incurred more serious damage with the increasing of freeze-thaw cycles; however their performance would be improved by fiber type and dosage. Mass loss rate of JPA (specimen with 2% volume content of JP fiber) was lower than JPB (specimen with 1% volume content of JP fiber). Furthermore, the mass loss rate of JPB was lower than that of CPB (specimen with 1% volume content of CP fiber). The longitudinal relative dynamic elastic modulus of JPA was higher than that of JPB while the longitudinal relative dynamic elastic modulus of JPB was higher than that of CPB. In addition, the compressive strength and flexural strength decreased with the increasing of freeze-thaw cycles. Mechanical behaviors of specimens with fiber exhibited better strength than specimens without fiber. Based on the SL 211-2006 code for the design of hydraulic structures against ice and freezing action, JPA and JPB specimens are adequate for use in severe cold regions, while specimen CPA and CPB can be used in cold regions, specimen JPC only can be used in warm regions.
Identifer | oai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/11362 |
Date | 27 June 2017 |
Creators | Ge, W., Cai, C., Ji, X., Ashour, Ashraf, DaFu, C., Wang, B. |
Source Sets | Bradford Scholars |
Language | English |
Detected Language | English |
Type | Article, Accepted Manuscript |
Rights | © 2017 ASTM International, West Conshohocken. This is an accepted manuscript of an article accepted for publication in the Journal of Testing and Evaluation 2017. https://doi.org/10.1520/JTE20160145 |
Page generated in 0.0016 seconds