Friction Stir Processing (FSP) of aluminium alloys has been used to modify and improve the microstructure and relevant properties of fusion welded aluminium alloys. The effect of FSP on MIG-Laser Hybrid (MLH) welded aluminium alloy 6082-T6 mechanical and microstructural properties has been studied in this research. The FSP process was used on 6mm thick aluminium alloy plates and a tool was designed specifically for FSP, and the effect of varying speeds was analysed before the final FSP welds were made. The effect of FSP was analysed by optical microscopy, tensile, microhardness and fatigue testing. The aim of the study was to determine whether the FSP process has a beneficial influence on the mechanical properties and metallurgical integrity of MIG-Laser Hybrid welded 6082-T6 aluminium alloy with varying gap tolerances. Three welding processes were compared, namely combined Friction Stir Processing on MIG-Laser hybrid process (FSP-MLH), MLH and Friction Stir Welding (FSW) as part of the analysis. (FSP was carried out on MLH components when it was found that FSP is not an entirely complete welding process but rather a finishing process per se.) The aim of this dissertation is to investigate the effects of the FSP process on the weld quality of MLH welded joints and also to compare this to individual processes like FSW and MLH. This investigation was undertaken in order to gain an understanding of the effect of these processes on fatigue performance and microhardness distribution on aluminium alloy 6082-T6 weld joints.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:nmmu/vital:9610 |
| Date | January 2007 |
| Creators | Mjali, Kadephi Vuyolwethu |
| Publisher | Nelson Mandela Metropolitan University, Faculty of Engineering, the Built Environment and Information Technology |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Masters, MTech |
| Format | xxxi, 229 leaves, pdf |
| Rights | Nelson Mandela Metropolitan University |