Nanoscaled-Al2O3 particles reinforced 1050 Aluminum composites by FSP were successfully fabricated in this study. The grain size of 1050 aluminum was obviously refined to about 0.5£gm by friction stir process(FSP), and there was a tendency that grain size decreased with increasing of Al2O3 content, where grain size of 0.84£gm was achieved with 24.7vol% of Al2O3. Nanoscaled-Al2O3 particles reinforced 1050 Al alloy by FSP revealed an excellent strengthening effect and excellent ductileity, Where hardness and UTS of the composite with 24.7vol% nanoscaled-Al2O3 particles were increased up to Hv113 and 310MPa respectively. The tensile result showed a 400% of increase in UTS comparing to the pure Al after FSP.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-1027105-165006 |
| Date | 27 October 2005 |
| Creators | Cheng, Yu-sheng |
| Contributors | none, none, none |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-1027105-165006 |
| Rights | unrestricted, Copyright information available at source archive |
Page generated in 0.0046 seconds