Fumed silica filler has long been used to structurally reinforce silicone elastomers. Unfortunately, the combination of as little as a few weight percent of untreated fumed silica nanoparticles [uFSN] with a siloxane polymer, such as PDMS, forms a difficult to process waxy solid admixture that even long periods of high shear mixing will not thin. In the course of the current work it was noted that after a period of storage certain solid admixtures would become viscous liquids when subjected to additional high shear mixing. It was further found that the required aging period could be decreased if the admixture storage temperature were increased. The only known interaction of PDMS and uFSN at moderate conditions is the adsorption of polymer on filler, and this interaction is also known to occur more quickly at higher temperature. This study examines the relationship between polymer adsorption and admixture liquefaction. Further, the mechanical properties of cured elastomers containing liquefied admixtures are examined to assess the degree of reinforcement that these materials afford.
Identifer | oai:union.ndltd.org:vcu.edu/oai:scholarscompass.vcu.edu:etd-1442 |
Date | 29 November 2012 |
Creators | Brooke-Devlin, Wayne |
Publisher | VCU Scholars Compass |
Source Sets | Virginia Commonwealth University |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | Theses and Dissertations |
Rights | © The Author |
Page generated in 0.0015 seconds