Obten??o e estudo de um comp?sito com matriz de resina poli?ster e carga de p? da casca de ovo de galinha

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-10-02T23:44:18Z
No. of bitstreams: 1
MicaelaDeFreitasAndrade_DISSERT.pdf: 2178407 bytes, checksum: c7e3c6bd92127a3aa87e92fb7d2fc5e4 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-10-09T21:08:28Z (GMT) No. of bitstreams: 1
MicaelaDeFreitasAndrade_DISSERT.pdf: 2178407 bytes, checksum: c7e3c6bd92127a3aa87e92fb7d2fc5e4 (MD5) / Made available in DSpace on 2017-10-09T21:08:28Z (GMT). No. of bitstreams: 1
MicaelaDeFreitasAndrade_DISSERT.pdf: 2178407 bytes, checksum: c7e3c6bd92127a3aa87e92fb7d2fc5e4 (MD5)
Previous issue date: 2017-07-28 / O uso de materiais comp?sitos tem crescido principalmente daqueles que apresentam res?duos na sua composi??o, uma vez que os impactos ambientais gerados com o mau destino desses materiais t?m preocupado a sociedade. Este trabalho apresenta o estudo e caracteriza??o de um material comp?sito obtido da mistura de matriz polim?rica de resina poli?ster e res?duos da casca de ovo de galinha. As cascas recolhidas foram secas e quebradas para a obten??o de tr?s granulometrias (fina, m?dia e grossa). As matrizes utilizadas foram ?s resinas poli?ster ortoft?lica e tereft?lica, escolhendo-se o percentual de res?duo de 100% em massa em rela??o ? matriz, em fun??o de testes preliminares para o diagn?stico da satura??o do comp?sito. Os corpos de prova foram constru?dos e submetidos a testes para caracteriz?-los atrav?s de suas propriedades t?rmicas (condutividade t?rmica, capacidade t?rmica, difusividade e resistividade), mec?nicas (resist?ncias ? tra??o, flex?o e impacto) e f?sicas (densidade, absor??o de umidade e envelhecimento). Como esperado, o comp?sito proposto apresentou menor resist?ncia mec?nica do que a matriz, caracterizando o res?duo como carga de enchimento. Desta forma, todas as formula??es do comp?sito apresentaram-se aplic?veis em estruturas que n?o requerem resist?ncia a grandes esfor?os. O comp?sito apresentou condutividade t?rmica superior ?s resinas matrizes para todas as formula??es, com condutividade t?rmica superior a 0,21 W/m.K, classificando-se como condutor t?rmico. A densidade aparente dos comp?sitos n?o apresentou varia??o significativa em rela??o ? resina. A maior qualidade do comp?sito estudado foi a diminui??o da quantidade de resina a ser utilizada, uma vez que a carga de p? de res?duo pode alcan?ar 100% em rela??o ? matriz, diminuindo-se o custo do material obtido para a fabrica??o de estruturas diversas. / The use of composite materials has grown mainly from those that present residues in their composition, since the environmental impacts generated by the bad destiny of these materials have worried society. This work presents the study and characterization of a composite material obtained from the mixture of polymer matrix of polyester resin and residues of chicken eggshell. The collected shells were dried and broken to obtain three granulometries (fine, medium and coarse). The matrices used were the orthophthalic and terephthalic polyester resins, being chosen the percentage of residue of 100% in mass in relation to the matrix, as a function of preliminary tests for the diagnosis of composite saturation. The test specimens were constructed and subjected to tests to characterize them through their thermal properties (thermal conductivity, thermal capacity, diffusivity and resistivity), mechanical (tensile strength, flexural and impact strength) and physical properties (density, moisture absorption and aging). As expected, the proposed composite presented lower mechanical resistance than the matrix, characterizing the residue as filling load. In this way, all the formulations of the composite were applicable in structures that do not require resistance to great efforts. The composite presented superior thermal conductivity to the matrix resins for all the formulations, with thermal conductivity superior to 0,21 W/m.K, being classified as thermal conductor. The apparent density of the composites did not show significant variation in relation to the resin. The higher quality of the composite studied was the reduction of the amount of resin to be used, since the residue dust load can reach 100% in relation to the matrix, reducing the cost of the material obtained for the manufacture of diverse structures.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/24013
Date28 July 2017
CreatorsAndrade, Micaela de Freitas
Contributors25094955420, Mota, Maria Kalionara de Freitas, 05095942470, Santos, Natanaeyfle Randemberg Gomes dos, 03047568499, Souza, Luiz Guilherme Meira de
PublisherPROGRAMA DE P?S-GRADUA??O EM ENGENHARIA MEC?NICA, UFRN, Brasil
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0022 seconds