Previous issue date: 2005 / Resumo: A excelente resistência do Zinco em diferentes ambientes corrosivos e sua habilidade em proteger o aço, fazem do aço galvanizado e eletrodepósitos, materiais comuns na indústria automotiva e de construção civil. Os substratos de aço galvanizado e eletrodepósitos de Zinco necessitam, no entanto, ser protegidos em ambientes altamente corrosivos por revestimentos orgânicos (pinturas).A má aderência do sistema Zinco/pintura faz com que a superfície do substrato de Zinco receba um pré-tratamento contendo Cromo relativamente barato e efetivo porém, tóxico ao homem e ao meio ambiente. Filmes poliméricos contendo silanos organofuncionais surgem como alternativa à substituição de pré-tratamento livre de Cromo hexavalente 'CR POT. +6¿, pois são moléculas que podem atuar como agente de acoplamento, promotores de adesão e como protetoras de superfície. A principal vantagem da sua utilização é a promoção da adesão entre materiais orgânicos (pinturas) e inorgânicos (metais). Os sistemas Galvanizado/Silano e Ligas eletrodepositadas/Silano, foram estudados nesta dissertação. Para tanto, técnicas como EIE (Espectroscopia de Impedância Eletroquímica), XPS (Espectrometria Fotoelétrica de Emissão de Raios-X), Ângulo de Contato e análises microscópicas foram utilizadas. A avaliação da resistência por barreira foi feita através da Espectroscopia de Impedância Eletroquímica em solução de 0,1 M de NaCI, comparando-se os desempenhos dos revestimentos. A cura induziu uma modificação importante nos diagramas de impedância, além de outras variáveis, como a concentração, o tempo de hidrólise, os tipos de silano e os substratos diferentes. Os resultados indicaram o Zn/Co revestido por VS e Zn/Fe revestido por 'gama¿-UPS como os sistemas mais promissores / Abstract: The Zinc' s excellent resistance, as used in differents corrosive environments, and its hability to protect steel, make galvanized steel (HDG) and Zinc electrodepositions very usual materiaIs in the automotive and construction industries. Galvanized steel and Zinc electrodepositions substrates need, however, to be protected from strongly corrosive environments by organic coatings (painting). Zinc/paint system weak adhesion results in a relatively cheap and effective zinc substrate pretreatment, however toxic to humam being, and also to the environment. Organofunctional silanes appear as an altemative to substitute this pretreatment, without making use of hexavalent chromium 'CR POT. +6¿), because they are bifuncional molecules that can act as adhesion promoters and surface protectors. The main benefit to employ them is to promote adhesion between organic (painting) and inorganic (metals) materiaIs. The GalvanizedlSilane and Electrodeposition Alloys/Silane systems had been studied in this essay. Techniques like EIS (Electrochemical Impedance Spectroscopy), XPS (X-Ray Emission Photoeletric Spectrometry), Contact Angle and microscopical analyses were used in this work. The barrier for resistance was evaluated through Electrochemical Impedance Spectroscopy in a 0,1M NaCI solution comparing coatings performances. Curing caused as importante modification in the impedance diagrams, as well as other variables like concentration, hydrolysis time, silane types and different substrates. The results indicate the Zn/Co alloy coated for VS and Zn/Fe alloy coated for 'gama¿-UPS as the systems most promising / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263596 |
| Date | 28 February 2005 |
| Creators | Santos, Marcia Cristina Gonçalves dos |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Freire, Celia Marina de Alvarenga, 1960-, Freire., Celia Marina de Alvarenga, Yoshida, Ines Valeria Pagotto, Ballester, Margarita |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 96p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds