This master´s thesis deals with hot dip galvanizing of steel constructions and their protection from corrosion. This work describes the origin of corrosion of steel and its corrosion in different areas and presents degreasing and pickling before hot dip galvanization. It describes possibilities of making zinc layer by the wet and draw method of hot dip galvanization. Furthermore, it puts forward reactions between zinc and iron, possible defects of the zinc layer and influence of the hot dip galvanizing on the steel constructions. The experimental part examines the influence of the hydrogen charging on the material and the time of the flux operation on the quality of layer. The work further analyses the changing of mechanical properties of steels Hardox 500 and Weldox 700 as a result of the hydrogen embrittlement during pickling by the hydrochloric acid.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:231404 |
Date | January 2014 |
Creators | Pometlo, Stanislav |
Contributors | Vyplašil, Evžen, Kubíček, Jaroslav |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0096 seconds