Mixed matrix nanocomposite membranes composed of a crosslinkable polyimide matrix and high-silica molecular sieve particles were developed for purifying natural gas. It was shown that ideal mixed matrix effects were not possible without sieve surface modification. A previously developed Grignard procedure was utilized to deposit magnesium hydroxide nanostructures on the sieve surface in order to enhance polymer adhesion. Analyses of Grignard-treated sieves pointed to the formation of non-selective voids within the surface deposited layer. These voids were suspected to lead to lower-than-expected membrane performance. In order to improve membrane transport, a reactive sizing procedure was developed to fill these voids with polyimide-miscible material. In a serendipitous discovery, as-received sieves--when treated with this reactive sizing procedure--resulted in nearly identical membrane performance as reactive-sized, Grignard-treated sieves. This observation lead to the speculation of a non-ideal transport mechanism in mixed matrix membranes.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/39465 |
| Date | 11 January 2010 |
| Creators | Ward, Jason Keith |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Detected Language | English |
| Type | Dissertation |
Page generated in 0.0014 seconds