On the effect of nitrogen, hydrogen and cooling rate on the solidification and pore formation in Fe-base and Al-base alloys

Experiments on the production of porous metallic materials were performed on Fe-base and Al-base alloys. The method involves dissolution of gases in the liquid state and solidification at various cooling rates. The alloy compositions were selected to induce solidification of primary particles intended to control the pore distribution. For the Fe-base alloys, nitrogen was introduced into the melt by dissolution of chromium nitride powder. Fe-Cr-Mn-Si-C alloys featuring M7C3 carbide particles were selected. For the Al-base alloys, hydrogen gas was dissolved into the melt by decomposition of water vapor. Al-Ti and Al-Fe alloys featuring primary Al3Ti and Al3Fe intermetallic particles, respectively, were considered. In the Fe-base alloys, a homogeneous distribution of gas pores through the specimens’ volume was obtained at high cooling rate (water quenching) and after introduction of external nucleating agents. In the case of the Al-base alloys, a good pore distribution was observed at all cooling rates and without addition of nucleating agents. Calculations of the variation of nitrogen (respectively hydrogen) solubility based on Wagner interaction parameters suggest that pore nucleation and growth occur during precipitation of the primary particles (M7C3 carbides, Al3Ti or Al3Fe intermetallics), due to composition changes in the melt and resultant supersaturation with gas atoms. Microscopic analyses revealed that the primary particles control the pore growth in the melt and act as barriers between adjacent pores, thereby preventing pore coalescence and promoting a fine pore distribution. Uniaxial compression testing of the porous Al-Ti and Al-Fe materials showed the typical compressive behavior of cellular metals. Further work is needed to improve the quality and reproducibility of the porous structures which can possibly be used in energy absorption or load-bearing applications. As a corollary result of the quenching of hypereutectic Fe-Cr-Mn-Si-C alloys in the experiments of synthesis of porous metals, a homogeneous featureless structure was observed in some parts of the samples, instead of the equilibrium structure of M7C3 and eutectic phases. Subsequent investigations on rapid solidification of Fe-base alloys at various alloy compositions and cooling rates led to the formation of a single-phase structure for the composition Fe-8Cr-6Mn-5Mo-5Si-3.2C (wt.%), at relatively low cooling rates (≈103 K/s) and for large sample dimensions (2.85 mm). The single phase, which is likely to be the hcp ɛ-phase, was found to decompose into a finely distributed structure of bainite and carbides at ≈600 °C. The annealed structure showed very high hardness values (850 to 1200 HV), which could be exploited in the development of high-strength Fe-base materials. / QC 20100809

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-4428
Date January 2007
CreatorsMakaya, Advenit
PublisherKTH, Materialens processvetenskap, Stockholm : KTH
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeDoctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess
RelationKTH/MSE ; 2007:27

Page generated in 0.0017 seconds