Indium nitride has many applications as a semiconductor. High quality films of indium nitride can be grown using Chemical Vapour Deposition (CVD) and Atomic Layer Deposition (ALD), but the availability of precursors and knowledge of the underlaying chemical reactions is limited. In this study the gas phase decomposition of a new indium precursor, N,N-dimethyl-N',N''-diisopropylguanidinate, has been investigated by quantum chemical methods for use in both CVD and ALD of indium nitride. The computations showed significant decomposition at around 250°C, 3 mbar indicating that the precursor is unstable at ALD conditions. A computational study of the surface chemical mechanism of the adsorption of trimethylindium and ammonia on indium nitride was also performed as a method development for other precursor surface mechanism studies. The results show, in accordance with experimental data, that the low reactivity of ammonia is a limiting factor in thermal ALD growth of indium nitride with trimethylindium and ammonia.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:liu-144426 |
| Date | January 2018 |
| Creators | Rönnby, Karl |
| Publisher | Linköpings universitet, Kemi |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0016 seconds