AlGaN/GaN metal–insulator–semiconductor high electron mobility transistors (MIS-HEMTs) are promising candidates for next generation high-efficiency and high-voltage power applications. The excellent physical properties of GaN-based materials, featuring high critical electric field and large carrier saturation velocity, combined to the high carrier density and large mobility of the two-dimensional electron gas confined at the AlGaN/GaN interface, enable higher power density minimizing power losses and self-heating of the device. However, the advent of the GaN-based MIS-HEMT to the industrial production is still hindered by technological challenges that are being faced in parallel. Among them, one of the biggest challenge is represented by the insertion of a gate dielectric in MIS-HEMTs compared to Schottky-gate HEMTs, which causes operational instability due to the presence of high-density trap states located at the dielectric/III-nitride interface or within the dielectric. The development of a gold-free ohmic contact technology is another important concern since the high-volume and cost-effective production of GaN-based transistors also depends on the cooperative manufacturing of GaN-based devices in Si production facilities, where gold represents an undesidered source of contamination. In fact, even though over the past years there have been multiple attemps to develop gold-free ohmic contacts, there is still no full understanding of the contact formation and current transport mechanism.
The first objective of this work was the investigation of a gold-free and low-resistive ohmic contact technology to AlGaN/GaN based on sputtered Ta/Al-based metal stacks annealed at low temperatures. A low contact resistance below 1 Ω mm was obtained using Ta/Al-based metal stacks annealed at temperatures below 600 °C. The ohmic behavior and the contact properties of contact resistance, optimum annealing temperature and thermal stability of Ta/Al-based contacts were studied. The nature of the current transport was also investigated indicating a contact mechanism governed by thermionic field emission tunneling through the AlGaN barrier. Finally, gold-free Ta/Al-based ohmic contacts were integrated in MIS-HEMTs fabricated on a 150 mm GaN-on- Si substrate, demonstrating to be a promising contact technology for AlGaN/GaN devices and revealing to be beneficial for devices operating at high temperatures.
The optimization of the MIS-gate structure in terms of trap states at the dielectric/III-nitride interface and inside the dielectric in MIS-HEMTs using atomic layer deposited (ALD) Al2O3 as gate insulator was the second focus of this work. First, the MIS-gate structure was improved by an O2 plasma surface preconditioning applied before the Al2O3 deposition and by an N2 postmetallization anneal applied after gate metallization, which significantly reduced trap states at the Al2O3/GaN interface and within the dielectric. Afterwards, the effectiveness of these treatments was demonstrated in Al2O3-AlGaN/GaN MIS-HEMTs by pulsed current–voltage measurements revealing improved threshold voltage stability. Lastly, it was shown that also the lower annealing temperatures used for the formation of Ta/Al-based ohmic contacts, processed before gate dielectric deposition, are beneficial in terms of trap states at the ALD-Al2O3/GaN interface, representing a new aspect to be considered when using an ohmic first fabrication approach.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:81276 |
| Date | 11 October 2022 |
| Creators | Calzolaro, Anthony |
| Contributors | Mikolajick, Thomas, Dadgar, Armin, Technische Universität Dresden, NaMLab gGmbH |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, doc-type:doctoralThesis, info:eu-repo/semantics/doctoralThesis, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 10.3390/ma15030791, 10.1109/ESSDERC53440.2021.9631788, 10.1002/pssa.202000585, 10.1088/1361-6641/ab8755 |
Page generated in 0.0025 seconds