Pure, MgO doped and B2C3 doped monocalcium, dicalcium, and tricalcium silicates were prepared with different glass contents. Characterization of the anhydrous materials was carried out using optical microscopy, infrared absorption spectroscopy, and X-ray powder diffraction. The hydration of these compounds was studied as a function of the glass contents. The hydration studies were conducted at 25°C. Water/solid ratios of 0.5, 1, 10, and 16 were used for the various experiments. The hydration behavior was monitored through calorimetry, conductometry, pH measurements, morphological developments by scanning electron microscopy, phase development by X-ray powder diffraction, and percent combined water by thermogravimetry. A highly sensitive ten cell pseudo-adiabatic microcalorimeter was designed and constructed for early hydration studies. Conductometry was found to be of great utility in monitoring the hydration of monocalcium silicate and the borate doped dicalcium silicates.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc332357 |
Date | 08 1900 |
Creators | Zgambo, Thomas P. (Thomas Patrick) |
Contributors | Daugherty, Kenneth E., Cohen, Menashi D., Tarter, James G., Schwartz, Martin, Desiderato, Robert, Theriot, L. J. |
Publisher | North Texas State University |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | xvi, 288 leaves: ill., Text |
Rights | Public, Zgambo, Thomas P. (Thomas Patrick), Copyright, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0015 seconds