Transient Shear Flow Rheology of Concentrated Long Glass Fiber Suspensions in a Sliding Plate Rheometer

Transient viscosity growth measurements at the startup of shear flow were performed on long glass fiber-filled polypropylene. Samples were prepared with fibers pre-oriented either in 1-direction, 3-direction or random in 1-3 plane, where the 1-direction is the direction of shear motion, the 2-direction is perpendicular to the shear plane and the 3-direction is the neutral direction. A sliding plate rheometer incorporating a shear stress transducer was constructed in the lab. It was shown that this device works well for the tested materials including a Newtonian oil, a low density polyethylene (LDPE) and short glass fiber-filled polypropylene. The transient viscosity growth behavior for long glass fiber suspensions was subsequently investigated. The results suggested that both, fiber length and fiber concentration have pronounced effect on the steady state suspension viscosity. It was also observed that the transient behavior of the pre-oriented samples was highly dependent on the initial orientation state of the fibers. / Master of Science

Identiferoai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/34784
Date21 September 2009
CreatorsAgarwal, Neeraj
ContributorsChemical Engineering, Baird, Donald G., Davis, Richey M., Wapperom, Peter
PublisherVirginia Tech
Source SetsVirginia Tech Theses and Dissertation
Detected LanguageEnglish
TypeThesis
Formatapplication/pdf
RightsIn Copyright, http://rightsstatements.org/vocab/InC/1.0/
RelationAgarwal_N_T_2009.pdf

Page generated in 0.0023 seconds