We report a method of increasing fracture toughness (KIc) and strain energy release rate (GIc) of vinyl-ester (VE) matrix by adopting a hybrid (dual) reinforcement strategy. The idea of using this strategy was to trigger intrinsic polymer-nanoparticle interaction such as carbon nanotube (CNT) pull-out and interface sliding to enhance energy absorption during fracture. Additionally, we included a second reinforcement, graphene nanoplatelets (GNP), to promote crack-deflection, crack bridging and cross-linking density. Both reinforcements were dispersed into the polymer in three states: non-functionalized (nf>); functionalized with COOH (f>); surface-treated with Triton X-100 (TX100). We embarked on numerous experiments with many combinations of these variables. We measured KIc and GIc using ASTM D5045-14. We conducted an exhaustive iterative investigation with three systems (f>CNT-VE; f>GNP-VE; f>CNT-f>GNP-VE) to determine the best weight-percentage for the nanocomposite system that produced the highest KIc and GIc values when compared to neat-VE. We found that 0.5wt% f>CNT with 0.25wt% f>GNP in the VE matrix resulted in the highest fracture toughness values and was termed the optimized hybrid nanocomposites (OHN) system. Subsequently, we explored further increasing the KIc and GIc of OHN through altering the nanoparticle surface characteristics, which led to four OHN groups: f>CNT-f>GNP-VE; f>CNT-f>GNP-TX100-VE; nf>CNT-nf>GNP-TX100-VE; nf>CNT-nf>GNP-VE. We discovered that the OHN group with non-functionalized nanofillers that were TX100 surface treated (0.5wt%nf>CNT-0.25wt%nf>GNP-TX100-VE) generated the greatest improvements in KIc and GIc.
Ultimately, we observed that the KIc of neat-VE increased by 65%, from 1.14 to 1.88 MPa*(m½). The improvement in GIc was even greater with an increase of 166%, from 370 to 985 J/(m2). Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) studies showed a minor shift in glass transition temperature (Tg) by up to 8°C when comparing neat-VE specimens to OHN specimens. A similar increase in maximum thermal decomposition temperature (Tp) of up to 8°C was observed through thermogravimetric analysis (TGA) and derivative TGA (DTG). Scanning electron microscope (SEM) studies revealed that the source of improvements in fracture toughness and thermal properties was primarily the three-dimensional hybrid nanostructures (3DHN) that formed by binding CNT and GNP together, which caused an increase in nanoparticle surface area and inhibited agglomerations. / Includes bibliography. / Dissertation (Ph.D.)--Florida Atlantic University, 2018. / FAU Electronic Theses and Dissertations Collection
| Identifer | oai:union.ndltd.org:fau.edu/oai:fau.digital.flvc.org:fau_40718 |
| Contributors | Gapstur, Christopher M. (author), Mahfuz, Hassan (Thesis advisor), Florida Atlantic University (Degree grantor), College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering |
| Publisher | Florida Atlantic University |
| Source Sets | Florida Atlantic University |
| Language | English |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation, Text |
| Format | 172 p., application/pdf |
| Rights | Copyright © is held by the author, with permission granted to Florida Atlantic University to digitize, archive and distribute this item for non-profit research and educational purposes. Any reuse of this item in excess of fair use or other copyright exemptions requires permission of the copyright holder., http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.002 seconds