Publics are facing a great challenge of infections from pathogens. Polyethylene terephthalate (PET) is widely used in health-care settings. It is vital to develop effective and regenerable antimicrobial PET. In this study, effective antibacterial modification of PET was achieved by immobilizing N-halamine biocide poly (N-chloroacrylamide) (PCA) onto PET through the formation of a surface interpenetrating network. The successful and uniform immobilization was confirmed by FTIR and XPS. The immobilization is durable to a 72 hours soxhlet extraction. Surface morphology of the fabrics did not significantly change after modification with IP less than 20%. The modified fabric can bring 100% reduction of 10e6 CFU/ml of several clinical important bacteria in 15 min contact. The regenerability of N-halamine on PAM modified PET was studied by FTIR, titration and N analysis. After 30 regeneration cycles, the PAM-DVB network modified PET was still able to provide 100% reduction of HA-MRSA in 20 min contact.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:MWU.1993/4083 |
| Date | 27 August 2010 |
| Creators | Zhao, Nan |
| Contributors | Liu, Song (Textile Sciences), Zhong, Wen (Textile Sciences) Freund, Michael (Chemistry) |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | en_US |
| Detected Language | English |
Page generated in 0.0024 seconds