The static and dynamic flexural properties of a wood fiber matrix internally reinforced with continuous glass fibers were investigated. When modelled as a sandwich composite, the static flexural modulus of elasticity (MOE) of glass fiber reinforced hardboard could be successfully predicted from the static flexural MOE of the wood fiber matrix, and the tensile MOE and effective volume fraction of the glass fiber reinforcement. Under the same assumption, the composite modulus of rupture (MOR) is a function of the reinforcement tensile MOE and effective volume fraction, and the matrix stress at failure. The composite MOR was predicted on this basis with limited success.
The static flexural modulus of elasticity, dynamic modulus of elasticity, and modulus of rupture of glass fiber reinforced hardboard increased with increasing effective reinforcement volume fraction. The logarithmic decrement of the composite decreased with increasing effective reinforcement volume fraction. Excellent linear correlation found among flexural properties determined in destructive static tests and nondestructive dynamic tests demonstrated the usefulness of dynamic test methods for flexural property evaluation.
The short-term flexural creep behavior of glass fiber reinforced hardboard was accurately described by a 4-element linear viscoelastic model. Excellent agreement existed between predicted and observed creep deflections based on nonlinear regression estimates of model parameters. / Ph. D.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/53596 |
| Date | January 1985 |
| Creators | Smulski, Stephen John |
| Contributors | Forestry and Forest Products, Ifju, Geza, Glasser, Wolfgang G., Wightman, James P., Kamke, Frederick A., Brinson, Halbert F. |
| Publisher | Virginia Polytechnic Institute and State University |
| Source Sets | Virginia Tech Theses and Dissertation |
| Language | en_US |
| Detected Language | English |
| Type | Dissertation, Text |
| Format | xviii, 167 leaves, application/pdf, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | OCLC# 13488815 |