Experimental Studies of Thermal Diffusivities concerning some Industrially Important Systems

The main objective of this industrially important work was to gain an increasing understanding of the properties of some industrially important materials such as CMSX-4 nickel base super alloy, 90Ti.6Al.4V alloy, 25Cr:6Ni stainless steel, 0.7% carbon steel, AISI 304 stainless steel-alumina composites, mould powder used in continuous casting of steel as well as coke used in blast furnace with special reference to the thermal diffusivities. The measurements were carried out in a wide temperature range covering solid, liquid, glassy and crystalline states. For CMSX-4 alloy, the thermal conductivities were calculated from the experimental thermal diffusivities. Both the diffusivities and conductivities were found to increase with increasing temperature. Microscopic analysis showed the presence of intermetallic phases γ´ such as Ni3Al below 1253 K. In this region, the mean free path of the electrons and phonons is likely to be limited by scattering against lattice defects. Between 1253 K and solidus temperature, these phases dissolved in the alloy adding to the impurities in the matrix, which, in turn, caused a decrease in the thermal diffusivity. This effect was confirmed by annealing the samples at 1573 K. The thermal diffusivities of the annealed samples measured at 1277, 1403 and 1531 K were found to be lower than the thermal diffusivities of non-annealed samples and the values did not show any noticeable change with time. It could be related to the attainment of equilibrium with the completion of the dissolution of γ´ phase during the annealing process. Liquid CMSX-4 does not show any change of thermal diffusivity with temperature. It may be attributed to the decrease of the mean free path being shorter than characteristic distance between two neighbouring atoms. Same tendency could be observed in the case of 90Ti.6Al.4V alloy. Since the thermal diffusivity increases with increasing temperature below 1225 K and shows slight decrease or constancy at higher temperature. For 25Cr:6Ni stainless steel, the thermal diffusivity is nearly constant up to about 700 K. Beyond that, there is an increase with temperature both during heating as well as cooling cycle. On the other hand, the slope of the curve increases above 950 K, which can be due to the increase of bcc phase in the structure. 0.7% carbon steel shows a decrease in the thermal diffusivity at temperature below Curie point, where the structure contains bcc+ fcc phases. Above this point the thermal diffusivity increases, where the structure contains only fcc phase. The experimental thermal conductivity values of these alloys show good agreement with the calculated values using Mills model. Thermal diffusivity measurements as a function of temperature of sintered AISI 304 stainless steel-alumina composites having various composition, viz, 0.001, 0.01, 0.1, 1, 2, 3, 5, 7, 8 and 10 wt% Al2O3 were carried out in the present work. The thermal diffusivity as well as the thermal conductivity were found to increase with temperature for all composite specimens. The thermal diffusivity/conductivity decreases with increasing weight fraction of alumina in the composites. The experimental results are in good agreement with simple rule of mixture, Eucken equation and developed Ohm´s law model at weight fraction of alumina below 5 wt%. Beyond this, the thermal diffusivity/ conductivity exhibits a high discrepancy probably due to the agglomeration of alumina particles during cold pressing and sintering. On the other hand, thermal diffusivities of industrial mould flux having glassy and crystalline states decrease with increasing temperature at lower temperature and are constant at higher temperature except for one glassy sample. The thermal diffusivity is increased with increasing crystallisation degree of mould flux, which is expected from theoretical considerations. Analogously, the thermal diffusivity measurements of mould flux do not show any significant change with temperature in liquid state. It is likely to be due to the silicate network being largely broken down. In the case of coke, the sample taken from deeper level of the pilot blast furnace is found to have larger thermal diffusivity. This can be correlated to the average crystallite size along the structural c-axis, Lc, which is indicative of the higher degree of graphitisation. This was also confirmed by XRD measurements of the different coke samples. The degree of graphitisation was found to increase with increasing temperature. Further, XRD and heat capacity measurements of coke samples taken from different levels in the shaft of the pilot blast furnace show that the graphitisation of coke was instantaneous between 973 and 1473 K. / QC 20100629

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-3864
Date January 2006
CreatorsAbdul Abas, Riad
PublisherKTH, Materialvetenskap, Stockholm : KTH
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeDoctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0018 seconds