The ZSM-12 zeolite is high silica material, with a one-dimensional pore structure that makes it presents a high performance as a catalyst in the hydroisomerization of hydrocarbons. For the synthesis of ZSM-12 in most cases, reagents are required that results in the process, for example, the use of organic agents drivers structure and / or a reactant to some sources have different values, the most interesting use which has the lowest value to make the synthesis more feasible in industrial scale. In this work we developed a synthesis route of zeolite ZSM-12 using a silica source more viable than the silica gel, sodium metassilicate. Samples were synthesized by the hydrothermal method at a temperature of 160 ° C using the following reagents: silica gel, sodium metassilicate, sodium hydroxide, pseudobohemita, tetraethylammonium hydroxide, sulfuric acid. After synthesis the samples were characterized by X-ray diffraction (XRD), absorption spectroscopy in the infrared (FT-IR), thermal analysis (TG / DTA), determination of surface area (BET) and scanning electron microscopy (MEV) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A ZSM-12 é uma zeólita rica em sílica, com uma estrutura de poros unidimensionais que faz com que ela apresente um grande desempenho como catalisador em reações de hidroisomerização de hidrocarbonetos. Para a síntese da ZSM-12, na maioria das vezes, são necessários reagentes que encarecem o processo, como por exemplo, o uso de agentes orgânicos direcionadores de estrutura ou/e algumas fontes de um reagente possuir valores diversos, sendo o mais interessante usar o que tem o valor mais baixo para tornar a síntese mais viável em escala industrial. No presente trabalho foi desenvolvida uma rota de síntese da zeólita ZSM-12 utilizando uma fonte de sílica mais viável que a sílica gel, o metassilicato de sódio. As amostras foram sintetizadas pelo método hidrotérmico à temperatura de 160°C, utilizando os seguintes reagentes: sílica gel, metassilicato de sódio, hidróxido de sódio, pseudobohemita, hidróxido de tetraetilamônio, ácido sulfúrico. Após as sínteses as amostras obtidas foram caracterizadas por difração de raios X (DRX), espectroscopia de absorção na região do infravermelho (FT-IR), análises térmicas (TG/DTA), determinação da área superficial (BET) e microscopia eletrônica de varredura (MEV).
Identifer | oai:union.ndltd.org:IBICT/oai:www.repositorio.ufal.br:riufal/1211 |
Date | 06 November 2012 |
Creators | Costa, Tiago Pereira Martins da |
Contributors | Silva, Antônio Osimar Sousa e, http://lattes.cnpq.br/5289388662589522, Urbina, Maritza Montoya, http://lattes.cnpq.br/0271592149131722, Sodré, Cristiane Holanda, http://lattes.cnpq.br/2425225506909155, Thiele, Daniel, http://lattes.cnpq.br/4254730962775391 |
Publisher | Universidade Federal de Alagoas, Brasil, Programa de Pós-Graduação em Engenharia Química, UFAL |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFAL, instname:Universidade Federal de Alagoas, instacron:UFAL |
Rights | info:eu-repo/semantics/openAccess |
Relation | bitstream:http://www.repositorio.ufal.br:8080/bitstream/riufal/1211/3/S%C3%ADntese+da+ze%C3%B3lita+ZSM-12+com+utiliza%C3%A7%C3%A3o+de+duas+fontes+de+s%C3%ADlica.pdf.txt, bitstream:http://www.repositorio.ufal.br:8080/bitstream/riufal/1211/2/license.txt, bitstream:http://www.repositorio.ufal.br:8080/bitstream/riufal/1211/1/S%C3%ADntese+da+ze%C3%B3lita+ZSM-12+com+utiliza%C3%A7%C3%A3o+de+duas+fontes+de+s%C3%ADlica.pdf |
Page generated in 0.0021 seconds