This work is devoted to study the influence of the composition on mechanical properties of high performance concret based on portland cement. 29 samples of high performance concrete (HPC) warying in composition were prepared. The constituents used for HPC preparation were: cement Aalborg White, silica fume, finelly ground blast furnace slag, finelly ground silica, calcinated bauxite and polycarboxylate based superplasticizer. The mechanical parameters (flexural and compressive strength) of the samples were observed after 7 and 28 days of moist curing. Compressive strength values after 28 days were in the range of 92 to 194 MPa and the flexural strength values were in the range of 7 to 23 MPa (without using of fiber reinforcement). The graphs showing mechanical parameters depending on the mixture composition were constructed and consequently evaluated.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216217 |
Date | January 2008 |
Creators | Veleba, Ondřej |
Contributors | Šoukal, František, Krátký, Josef |
Publisher | Vysoké učení technické v Brně. Fakulta chemická |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0062 seconds