The oxidation of three different steels used in the construction of petroleum refineryheaters was investigated by using thermogravimetric analysis technique (TGA). C-5,P-11, and P-22 steel samples were tested in two different oxidizing environments / air and CO2+N2+H2O (that simulates the combustion products of natural gas) at two different temperatures / 450oC and 500oC. In air oxidation P-22 had the best oxidation resistance among the three steels at two temperatures. In CO2+N2+H2O environment,C-5 possessed better oxidation resistance than P-22 and P-11. Analyses of oxidation products by using optical microscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM) were carried out to correlate TGA results to oxide
composition and morphology. Lower oxidation rate of P-22 in air was explained with reference to the formation of Cr-O phase. Analytical rate equations showed that all
the steels obeyed parabolic rate equation during oxidation and no transition was observed
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12606204/index.pdf |
| Date | 01 July 2005 |
| Creators | Sultan, Abdelrahman Saleh |
| Contributors | Karakaya, Ishak |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0019 seconds