The application of glass fiber reinforced composites has grown rapidly due to their high strength-to-weight ratio, low cost, and chemical resistance. However, the increasing demand for fiber reinforced composites results in the generation of more composite wastes. Mechanical recycling is a cost-effective and environmentally-friendly recycling method, but the loss in the quality of recycled glass or carbon fiber composite hinders the wide-spread use of this recycling method. It is important to develop novel composite materials with higher recyclability. Thermotropic liquid crystalline polymers (TLCPs) are high-performance engineering thermoplastics, which have comparable mechanical performance to that of glass fiber. The TLCP reinforced composites, called in situ composites, can form the reinforcing TLCP fibrils during processing avoiding the fiber breakage problem.
The first part of this dissertation is to study the influence of mechanical recycling on the properties of injection molded TLCP and glass fiber (GF) reinforced polypropylene (PP). The processing temperature of the injection molding process was optimized using a differential scanning calorimeter (DSC) and a rheometer to minimize the thermal degradation of PP. The TLCP and GF reinforced PP materials were mechanically recycled up to three times by repeated injection molding and grinding. The mechanical recycling had almost no influence on the mechanical, thermal, and thermo-mechanical properties of TLCP/PP because of the regeneration of TLCP fibrils during the mold filling process. On the other hand, glass fiber/PP composites decreased 30% in tensile strength and 5% in tensile modulus after three reprocessing cycles. The micro-mechanical modeling demonstrated the deterioration in mechanical properties of GF/PP was mainly attributed to the fiber breakage that occurred during compounding and grinding.
The second part of this dissertation is concerned with the development of recyclable and light weight hybrid composites through the use of TLCP and glass fiber. Rheological tests were used to determine the optimal processing temperature of the injection molding process. At this processing temperature, the thermal degradation of matrix material was mitigated and the processability of the hybrid composite was improved. The best formulation of TLCP and glass fiber in the composite was determined giving rise to the generation of a recyclable hybrid composite with low melt viscosity, low mechanical anisotropy, and improved mechanical properties.
Finally, TLCP reinforced polyamide composites were utilized in an additive manufacturing application. The method of selecting the processing temperature to blend TLCP and polyamide in the dual extrusion process was devised using rheological analyses to take advantage of the supercooling behavior of TLCP and minimize the thermal degradation of the matrix polymer. The composite filament prepared by dual extrusion was printed and the printing temperature of the composite filament that led to the highest mechanical properties was determined. Although the tensile strength of the TLCP composite was lower than the glass fiber or carbon fiber composites, the tensile modulus of 3D printed 60 wt% TLCP reinforced polyamide was comparable to traditional glass or carbon fiber reinforced composites in 3D printing. / Doctor of Philosophy / The large demand for high performance and light weight composite materials in various industries (e.g., automotive, aerospace, and construction) has resulted in accumulation of composite wastes in the environment. Reuse and recycling of fiber reinforced composites are beneficial from the environmental and economical point of view. However, mechanical recycling deteriorates the quality of traditional fiber reinforced composite (e.g., glass fiber and carbon fiber). There is a need to develop novel composites with greater recyclability and high-performance.
Thermotropic liquid crystalline polymers (TLCP) are attractive high performance materials because of their excellent mechanical properties and light weight. The goal of this work is to generate recyclable thermotropic liquid crystalline polymer (TLCP) reinforced composites for use in injection molding and 3D printing. In the first part of this work, a novel recyclable TLCP reinforced composite was generated using the grinding and injection molding. Recycled TLCP composites were as strong as the virgin TLCP composites, and the mechanical properties of TLCP composites were found to be competitive with the glass fiber reinforced counterparts. In the second part, a hybrid TLCP and glass fiber reinforced composite with great recyclability and excellent processability was developed. The processing conditions of injection molding were optimized by rheological tests to mitigate fiber breakage and improve the processability. Finally, a high performance and light weight TLCP reinforced composite filament was generated using the dual extrusion process which allowed the processing of two polymers with different processing temperatures. This composite filament could be directly 3D printed using a benchtop 3D printer. The mechanical properties of 3D printed TLCP composites could rival 3D printed traditional fiber composites but with the potential to have a wider range of processing shapes.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/103439 |
| Date | 21 May 2021 |
| Creators | Chen, Tianran |
| Contributors | Chemistry, Baird, Donald G., Bortner, Michael J., Case, Scott W., Martin, Stephen Michael, Barone, Justin Robert |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Dissertation |
| Format | ETD, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.0023 seconds