ABSTRACT
SYNTHESIS AND CHARACTERIZATION OF ETHANOL ELECTRO-OXIDATION CATALYSIS
Demir-Kivrak, Hilal
Ph.D., Department of Chemical Engineering
Supervisor : Prof. Dr. Deniz Ü / ner
Co-supervisor : Dr. Sadig Kuliyev
October 2010, 196 pages
In this study, the role of defects, the role of Sn in relation to defects, and the role of oxide phase of tin in ethanol electro-oxidation reaction were investigated. Firstly, adsorption calorimetry measurements were conducted on monometallic (1%Pt, 2%Pt, and 5%Pt) and bi-metallic (5% Pt-Sn) &gamma / -Al2O3 supported Pt catalysts. It was observed that while saturation coverage values decreased, intermediate heats remained same for Pt-Sn catalysts by the increasing amount of tin. The effect of particle size was investigated on Pt/C (pH=5), Pt/C (pH=11) catalysts at different scan rates. At high scan rates (quite above diffusion limitations), current per site activities were nearly the same for 20% Pt/C (E-Tek), Pt/C (pH=11), and Pt/C (pH=5) catalysts, which explained as electro-oxidation reaction takes place at the defects sites. Furthermore, the effect of support on ethanol electro-oxidation was investigated on CNT supported Pt catalyst. Results indicate that only the metal
v
dispersions improved ethanol electro-oxidation reaction and support did not have any effect on ethanol electro-oxidation reaction. Results on the 20% Pt-Sn/C (15:1 to 1:1 Pt: Sn atomic ratios) and 20% Pt-SnO2/C (6:1 and 1:1) catalysts indicated that ethanol electro-oxidation activity increased by increasing tin amount. For 20% Pt-Sn/C catalysts, Pt-Sn (6:1)/C indicated best activity. On the other hand, 20% Pt-SnO2 (6:1)/C catalyst was better than Pt-Sn (6:1)/C in terms of ethanol electro-oxidation activity due to the fact that there was low contact between Pt and tin oxide particles.
Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12613887/index.pdf |
Date | 01 October 2010 |
Creators | Demir-kivrak, Hilal |
Contributors | Uner, Deniz |
Publisher | METU |
Source Sets | Middle East Technical Univ. |
Language | English |
Detected Language | English |
Type | Ph.D. Thesis |
Format | text/pdf |
Rights | To liberate the content for public access |
Page generated in 0.0017 seconds