Orientador: Oswaldo Luiz Alves / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-13T13:21:45Z (GMT). No. of bitstreams: 1
Oliveira_FlavioHenrique_M.pdf: 1865644 bytes, checksum: f0716bfd25ded49ec69dd8796c111a00 (MD5)
Previous issue date: 2009 / Resumo: Sistemas ternários tipo hidrotalcita contendo metais de transição Ni, Fe e Cu tendo o ânion interlamelar o carbonato foram preparados através de um estudo sistemático de composição e parâmetros de síntese. Diferentes quantidades de Cu foram introduzidas na camada tipo brucita da hidrotalcita, sendo estas quantidades de 10, 20, 30, 40 e 50 % em relação a quantidade de Níquel. De acordo com difratogramas para baixas quantidades de cobre (10 e 20 %) a fase hidrotalcita apresentou-se pura, para maiores quantidades de cobre ocorreu segregação de fase a qual foi identificada como CuO. A preparação dos compostos ternários foi feita tendo como razão de metal II para metal III 2:1, essa razão entre os metais foi confirmada através de análises de ICP a qual demonstrou exata proporção entre os metais nas amostras. Análise térmica apresentaram um comportamento típico para hidrotalcitas, apresentando duas transições características a 170 °C e a 280 ºC. Devido à ocorrência de alta segregação de fases que ocorre na precipitação com estes metais, foram realizados experimentos com diferentes temperaturas de precipitação e os resultados preliminares indicam a formação de uma fase pura em baixas temperaturas. Compostos preparados com 30 % de Cu a temperatura ambiente apresenta segregação de fase o que não ocorre a temperaturas próximas a 0 ºC, temperaturas elevadas (60 °C) favorecem a formação de óxidos durante a precipitação. Portanto baixas temperaturas de precipitação resultam em fases puras de hidrotalcitas para concentrações de cobre intermediarias, como conseqüência é possível preparar amostras com altas concentrações de cobre na estrutura lamelar com a fase da hidrotalcita pura. Com estes metais de transição na estrutura lamelar este sistema pode vir a ser um bom precursor na formação de óxidos dos respectivos metais que constituem o composto, com a finalidade de ser utilizada em catálise / Abstract: Ternary systems of hydrotalcite-like compouds containing transition metals Ni, Fe and Cu and the interlayer anion the carbonate were prepared through a systematic study of composition and synthesis parameters. Different amounts of Cu were introduced into the layer hydrotalcite, and the figure of 10, 20, 30, 40 and 50% on the amount of Nickel. According to difratograms, for low quantities of copper (10 and 20%) the phase is pure hydrotalcite and for larger quantities of copper segregation occurred, which was identified as CuO. The preparation of ternary compound was made with the ratio of metal II to metal III 2:1, the ratio between the metals was confirmed through analysis of ICP which showed exact proportion between the metals in the samples. Thermal analysis showed a typical behavior for hydrotalcite, presenting features two transitions to 170 ° C and 280 C. Due to the high occurrence of segregation of phases in the precipitation that occurs with these metals, experiments were performed with different temperatures and precipitation and the preliminary results indicate the formation of a pure phase at low temperatures. Compounds prepared with 30% of Cu at room temperature shows segregation of the stage that does not occur at temperatures close to 0 º C, high temperature (60 C) favor the formation of oxides during the precipitation. In conclusion, low temperatures of precipitation result in phases of pure hydrotalcite for an intermediary concentration of copper, as a result, is possible to prepare samples with high concentrations of copper in the lamellar structure with pure phase of hydrotalcite. With these transitions metals in the lamellar structure this systems might be a good precursor in the formation of oxides of the metals that constitute the compound in order to be used in catalysis / Mestrado / Quimica Inorganica / Mestre em Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/249014 |
| Date | 02 October 2009 |
| Creators | Oliveira, Flavio Henrique |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Alves, Oswaldo Luiz, 1947-, Rubira, Adley Forti, Longo, Cláudia |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 62f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0033 seconds