1 Abstract The structure of layered zinc hydroxide intercalated with dodecyl sulfate (LZH-DS) anions was studied in detail. LZH-DS was prepared by direct precipitation in water and formed different phases. The following phases of LZH-DS were prepared - "extended" phase (ex) by direct precipitation in water, "shrunk" (s) and "super-shrunk" (ss) phases via treatment of LZH-DS(ex) phase in methanol. The studies of the thermal behavior of LZH-DS(ex) revealed interstratification of intercalated DS anions. It is the first example of interstratification in layered hydroxides that are intercalated with long aliphatic alkyl chain anions. The experimental results were used for molecular dynamic modelling of the structures. Nanometric thin films were prepared by dip-coating and inkjet printing of ZnO nanosheets on glass plates. The side-by-side alignment of the ZnO nanosheets on the substrate resulted in thin, transparent, oriented ZnO surfaces with the high-energy {001} facets exposed. The method of nanosheet deposition affected the film morphology; the dip-coated films were smooth and nonporous, while the inkjet-printed films were rough and had a surface area in the range of approximately 100-160 m2 g-1 . The first-order rate constants for the photocatalytic degradation of 4-chlorophenol on the nanosheet-based films...
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:338742 |
Date | January 2014 |
Creators | Hynek, Jan |
Contributors | Lang, Kamil, Kovanda, František |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0017 seconds