Nitrogen Without Oxygen : The effect of ferroalloys added after vacuum treatment on cleanliness of nitrogen-alloyed tool steel

Nitrogen-alloyed tool steel is made at Uddeholms AB by adding high-nitrogen ferroalloy after vacuum degassing where introduced impurities are hard to remove. In this thesis two types of high-nitrogen ferrochromium are compared, a solid version and a powder cored wire. They are examined in crossection and 16 samples from four charges are examined with Pulse Distribution Analysis as well as systematic microscopy of polished cross sections. The PDA results missed smaller spinel inclusions shown in previous research to be detrimental. The wire form shows promise but more charges need to be evaluated before a conclusion is drawn. / Kvävelegerat verktygsstål tillverkas hos Uddeholms AB genom tillsats av kväverika ferrolegeringar efter vakumavgasning, och orenheter som introduceras i detta steg är svåra att avskilja. I den har uppsatsen jämförs två typer av kväverikt ferrokrom varav en i form av stycken och en i form av tråd med pulverkärna. De undersöks i tvärsnitt och totalt 16 prov från fyra charger undersöks med PDA (pulsfördelningsanalys) och systematisk mikroskopering i tvärsnitt. Resultaten från PDA missade mindre inneslutningar av spinell vilka tidigare har visat sig problematiska. Trådformen verkar lovande men fler charger behöver undersökas för att kunna dra en definitiv slutsats.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-298093
Date January 2021
CreatorsNilsson Hultén, Leo
PublisherKTH, Materialvetenskap
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageSwedish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess
RelationTRITA-ITM-EX ; 2021:443

Page generated in 0.0024 seconds