Esta tese aborda quatro tópicos fundamentais para o desenvolvimento e aplicação de membranas eletroativas nanoestruturadas (MENs): (i) síntese e caracterização de nanopartículas (Nps) de prata, ouro e platina encapsuladas em moléculas de dendrímero poliamidoamina geração 4 (PAMAM); (ii) preparação de filmes automontados contendo PAMAM e Nps de ouro (PAMAM-Au); (iii) preparação de MENs utilizando sistema core-shell PAMAM-Au@Me, onde Me é um mediador redox; (iv) imobilização enzimática em MENs e estudos biocatalíticos associados a processos eletroquímicos. As Nps foram caracterizadas observando-se a banda plasmônica em espectros na região do UV-Vis. Imagens de microscopia eletrônica de transmissão revelaram que PAMAM-Au e PAMAM-Pt possuem morfologias esféricas, enquanto o PAMAM-Ag forma grandes cristais com estruturas fractais. Estruturas cúbicas de face centrada caracterizaram os cristais formados de Au e Pt, sendo possível estimar os diâmetros (3,0 nm) das Nps pela equação de Scherrer em difratogramas de raios X, confirmados posteriormente por microscopia eletrônica por transmissão (TEM). Um indício de estabilização por encapsulamento do híbrido PAMAM-Au foi obtido de espectros de infravermelho (FTIR), a partir de modificações nas bandas das amidas. A cinética de reação para formação de PAMAM-Au também foi estudada. Filmes de PVS/PAMAM-Au (onde PVS é o poli(ácidovinilssulfônico)) foram preparados com 5 minutos de imersão, com a mesma quantidade de material sendo adsorvida em cada camada, segundo medidas de espectroscopia UV-Vis e voltametria cíclica (CV). No caso do eletrodo ITO-(PVS/PAMAM-Au), saltos de elétrons foram considerados o mecanismo de transporte de carga ao longo do filme. Um novo sistema core-shell Au@PB foi preparado, formando um sistema ITO-(PVS/PAMAM-Au)6@PB, em que a eletrodeposição de PB (azul da Prússia) foi monitorada medindo-se as correntes faradaicas durante os ciclos potenciodinâmicos. Outros mediadores de hexacianoferratos de metais de transição (Fe, Ni, Co e Cu) foram obtidos sobre eletrodos de ITO-(PVS/PAMAM-Au). De resultados de espectroscopia de impedância eletroquímica (EIS), verificou-se que a resistência de transporte de carga decresce na sequência CuHCF > FeHCF > NiHCF > CoHCF e todos os eletrodos apresentaram atividade catalítica para o peróxido de hidrogênio. Uma nova configuração de eletrodo, ITO-(PVS/PAMAM-Au)3@CoHCF-GOx, pôde ser aplicada como dispositivo enzimático, com a glicose oxidase (GOx) sendo imobilizada por drop-coating na superfície do eletrodo e aplicada em experimentos de biocatálise. A glicose pôde ser detectada a 0,0 V (Ag/AgCl), com resposta linear até 100 µmol L-1 de glicose, sensibilidade de 115 nA mmol L-1, limite de detecção de 5,5 µmol L-1 e KMapp de 0,24 mmol L-1, mostrando que o sistema aqui proposto cria um ambiente propício para a enzima operar com alta atividade catalítica. / This thesis addresses four fundamental topics for producing and applying electroactive nanostructured membranes (ENMs): (i) synthesis of Au, Pt and Ag nanoparticles (Nps) using polyamidoamine (PAMAM generation 4) dendrimers as template/stabilizers; (ii) fabrication of layer-by-layer (LbL) films comprising PAMAM with AuNps (PAMAM-Au) and poly(vinylsulfonic acid) (PVS); (iii) preparation of a new core-shell system with Prussian blue (PB) around the Au nanoparticles (PAMAM-Au@PB); (iv) enzyme immobilization on ENMs and bioelectrochemistry studies. The formation of the Nps inside PAMAM was monitored by measuring the plasmonic band of NPs via UV-Vis spectroscopy. Images from transmission electron microscopy (TEM) showed well-organized Au and Pt spherical particles, with average diameter of 3 nm and narrow size distribution. In addition, X-ray diffraction of Nps enabled easy identification of the Nps atomic planes (face-centered cubic arrangements). However, PAMAMAg growth showed fractals structures. In order to confirm Au NPs encapsulation inside the PAMAM dendrimer, FTIR spectra in the transmission mode for neat PAMAM and PAMAM-Au were compared. The kinetics of formation of PAMAM-Au was studied by UV-Vis spectroscopy. The deposition of individual PAMAM-Au layers was examined in detail: the adsorption kinetics was determined by CV to be first-order and that 5 min of adsorption was sufficient for maximum coverage. Formation of PVS/PAMAM-Au multilayers showed a linear increase in anodic and cathodic peak currents, indicating that the same amount of material was adsorbed in each deposition step. Electron-hopping was inferred as the charge transport mechanism between PAMAM-Au layers. Using hexacyanoferrate (III) to probe the electrochemical reaction at the electrode surface, the charge transport in the PAMAM-Au layers was shown to be faster than for non-modified electrodes. A new system based on PAMAM-Au@PB was prepared by simple potential cycling electrodeposition after ITO-PVS/PAMAM-Au LbL film preparation. New systems are described based on ENM membranes of ITOPVS/ PAMAM-Au LbL electrodes, with a redox mediator (Me) electrodeposited around Au nanoparticles. The resulting ITO-PVS/PAMAM-Au@Me system was then characterised electrochemically using cyclic voltammetry and electrochemical impedance spectroscopy. We demonstrated that the concept of ENM can be generalized to a wider variety of redox mediators. All electrodes modified with hexacyanoferrates showed electrocatalytic activity towards hydrogen peroxide, which is promising for the preparation of nanodevices requiring redox mediators. An electrochemical enzyme device with glucose oxidase (GOx) immobilized at ITO-(PVS/PAMAM-Au)3@CoHCF ENM was developed. Using CoHCF as redox mediator, hydrogen peroxide (the enzymatic reaction product) was determined at 0.0 V (vs. SCE), with linear range up to 100 Zmol L-1 of glucose, sensitivity of 115 nA mmol L-1, detection limit of 5.5 Zmol L-1 and KM app of 0.24 mmol L-1. Such a performance indicates that this system promotes a friendly environment for enzyme immobilization.
| Identifer | oai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-25102007-111702 |
| Date | 26 February 2007 |
| Creators | Frank Nelson Crespilho |
| Contributors | Francisco Carlos Nart, Orlando Fatibello Filho, Ubirajara Pereira Rodrigues Filho, Susana Ines Cordoba de Torresi, Maria Elisabete Darbello Zaniquelli |
| Publisher | Universidade de São Paulo, Físico-Química, USP, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP |
| Rights | info:eu-repo/semantics/openAccess |