Orientador: Jose Claudio Moura / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-20T13:39:30Z (GMT). No. of bitstreams: 1
KaskantzisNeto_Georges_D.pdf: 4435443 bytes, checksum: b3a0ade930d162030b80eaa7d80d859a (MD5)
Previous issue date: 1995 / Resumo: Este trabalho é um estudo da oxidação do hidrogênio sobre catalisadores de Paládio suportados em Alumina. Foi utilizado um catalisador preparado no laboratório através da impregnação do sal precursor 'PD¿CL IND. 2¿ em Alumina extrudada e sintetizada. A decomposição do sal depositado no suporte foi feita através de tratamento térmico à '400 GRAUS¿C e ativação por redução com hidrogênio à '300 GRAUS¿C. Foi também utilizado um catalisador industrial de Paládio suportado em Alumina. Foram coletados dados cinéticos em uma instalação de bancada, contendo um reator de leito fixo, imerso em um banho termostático de óleo de silicone. A coleta dos dados cinético foi feita na faixa de temperatura de 80 a '150 GRAUS¿C, razões molares hidrogênio/oxigênio de 199,99 e 65.66 e vazões de 200 a 1200 N ml/min de mistura reagente. A interpretação dos dados foi realizada diferencial de análise, determinando-se as taxas de reação através da técnica spline acoplada ao método da máxima verossimilhança e aplicou-se o método das taxas iniciais para discriminar mecanismos de reação. O método integral de análise foi empregado para se determinar as constantes cinéticas da equação da taxa de oxidação do hidrogênio. Foi utilizado um mecanismo de reação e a sistemática de Temkin para estabelecer a equação da taxa de oxidação do hidrogênio sobre os catalisadores citados... Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: The work presents the study of oxidation of hidrogen over Pallladium supported on Alumina. The catalyst was prepared by impregnation of the precursor salt 'PD¿¿CL IND. 2¿ on Alumina particles sized by extrusion and sintering. The salt decomposing at the surface was done by thermal treatment at the temperature of '400 DEGREES¿C followed by reduction with hydrogen at '300 DEGREES¿C. An industrial catalysts of Palladium supported on Alumina was used too. The kinetic data was collected on a bench scale experimental set up involving a fixed bed tubular reactor immersed on an agitated oil bath. The kinetic data measurements covered a temperature range from 80 to '150 DEGREES¿C, a molar ratio of hydrogen;oxygen of 199, 99, 65.66 with flow rate from 200 to 1200 N ml/min. The kinetic data analysis was made by differential method and the rates of reaction stabilished by spline technique coupled with the maximum likelihood principle and the method of initial rates was applied too. The integral method was employed to determinate the kinetics constants of the reaction rate equation for oxidation of hydrogen. A mechanism of reaction was proposed utilizing Temkin method and the reaction rate was deduced for the catalytic oxidation of hydrogen... Note: The complete abstract is available with the full electronic digital thesis or dissertations / Doutorado / Desenvolvimento de Processos Químicos / Doutor em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266249 |
| Date | 29 May 1995 |
| Creators | Kaskantzis Neto, Georges |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Moura, José Claudio, 1943-, D'Avila, Saul Gonçalves, Maciel Filho, Rubens, Giulietti, Marco, Kaminski, Moacir |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 134f., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds