Orientador: Anselmo Eduardo Diniz / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-28T12:31:16Z (GMT). No. of bitstreams: 1
Loureiro_Daniel_M.pdf: 3345826 bytes, checksum: a140e145cbae9ae1a5f3f14eaee94c0f (MD5)
Previous issue date: 2015 / Resumo: As ligas de níquel são utilizadas em diversos setores industriais sempre que há necessidade de se associar elevada resistência mecânica com resistência à corrosão, ao desgaste e à oxidação. No entanto, as ligas de níquel apresentam baixa usinabilidade, implicando em processos relativamente ineficientes nos quais o desgaste da ferramenta e a integridade superficial são os principais fatores limitantes. A baixa usinabilidade destas ligas está relacionada com as suas características inerentes, tais como: alta dureza e resistência mecânica a quente, altas tensões de cisalhamento durante o processo de corte, alta taxa de encruamento, presença de carbonetos abrasivos na matriz, baixa condutividade térmica e soldagem da peça e da aresta de corte. Dentre as ligas de níquel, uma que apresenta propriedades desejadas para a indústria de exploração de petróleo é a liga 625. O objetivo do presente trabalho é a verificação da integridade da superfície usinada da liga 625, pela caracterização através da rugosidade, microestrutura, microdureza Vickers da superfície e da subsuperfície e da tensão residual de oito diferentes superfícies torneadas com diferentes geometrias da ferramenta (positiva e negativa) e diferentes condições de usinagem. Neste trabalho foram avaliados os danos que o torneamento em condições de acabamento proporciona à superfície usinada e que podem resultar em variação da resistência à corrosão e à fadiga. Dentre os principais resultados destaca-se aquele que aponta que as superfícies torneadas com geometria positiva da ferramenta produziram tensões compressivas na superfície, enquanto aquelas torneadas com ferramentas negativas produziram tensões trativas na superfície / Abstract: The nickel alloys are used in many industrial sectors where there is a need to associate high mechanical strength with resistance to corrosion, wear and oxidation. However, nickel alloys have poor machinability, resulting in relatively inefficient process wherein tool wear and surface integrity are the limiting primary factors. The low machinability of these alloys is related to their inherent characteristics, such as hot hardness and mechanical resistance, high shear rates during the cutting process, high work hardening rate, presence of abrasive carbides in the matrix, low thermal conductivity and welding the workpiece and cutting edge. Among the nickel alloys, one that has desired properties to the oil exploration industry is the alloy 625. The aim of this work is the check of the surface integrity through the characterization by roughness, microstructure, microhardness of the surface and sub- surface and residual stress, of eight turned different surfaces with different geometries tool (positive and negative) and machining conditions. This study evaluated the damage that finish conditions provides to the machined surface and witch can result in variations of resistance to corrosion and fatigue. Among the main results stands out the one who points out that turned surfaces with positive tool geometry produced compressive residual stresses on the surface, while those with negative turned tools produced tensile residual stresses on the surface / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265754 |
| Date | 28 August 2018 |
| Creators | Loureiro, Daniel, 1986- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Diniz, Anselmo Eduardo, 1959-, Fogagnolo, João Batista, Delijaicov, Sergio |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 82 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds