The doctoral thesis is aimed at preparation of glass fiber reinforced polymer composites with controlled interphase formed by plasma-polymerized tetravinylsilane and tetravinylsilane/oxygen thin films. The thin polymer films of specific physico-chemical properties and thickness were deposited to improve interfacial adhesion of glass fiber/polyester composites. The fiber surface modification was performed by using plasma enhanced chemical vapor deposition in low-temperature RF plasma operating in an various effective power range and different treatment time. Test results were examined in relation to the interlayer thickness and different treatment conditions. The prepared interlayers were analyzed to evaluate physico-chemical composition and properties (XPS, RBS, ERDA, FTIR and spectroscopic elipsometry). Selected mechanical properties were evaluated by AFM. Mechanical response of plasma interlayers was evaluated by short beam shear test and direct method of testing the interfacial shear strength using microindentation. The interphase shear failure was controlled by the shear strength at the interlayer/fiber interface as follows from experimental and model data.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:261220 |
| Date | January 2016 |
| Creators | Knob, Antonín |
| Contributors | Marek,, Aleš, Burša, Jiří, Čech, Vladimír |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0017 seconds