Previous issue date: 2016-03-04 / FACEPE / O Poli (etileno-co-acetato de vinila), EVA, é um copolímero da família das olefinas. É obtido
por meio da polimerização em cadeia via radical livre, usualmente utilizando oxigênio e/ ou
peróxidos orgânicos para a geração de radicais iniciadores da polimerização do etileno e do
acetato de vinila, à alta temperatura e pressão. Seu uso varia de acordo com o teor de acetato de
vinila na sua composição e entre suas utilidades estão o seu uso na composição de
embalagens plásticas flexíveis para alimentos irradiados e revestimento para cabos elétricos.
Diante disso, é importante analisar os efeitos causados pela radiação gama nestas embalagens
e nos revestimentos destes cabos. Neste trabalho, a investigação dos efeitos da irradiação
gama no EVA foi dividida em duas partes: a primeira para doses mais baixas, entre 5 e
30kGy, utilizadas na irradiação de alimentos e radioesterilização de artefatos médicos,
utilizando filmes de EVA com 25% e 40% de acetato de vinila em sua composição. E a
segunda para doses mais altas, (doses de 250 -1000kGy), nas quais os cabos elétricos
utilizados em usinas nucleares são expostos, utilizando o EVA a 12%, 25% e 40% em
formato de pellets. Para a primeira parte foram preparados 12 filmes de EVA a 25% e 18
filmes de EVA a 40% pelo método casting film sendo, para o EVA a 40% foram preparados
três filmes para cada doses: 5kGy, 10kGy, 15kGy, 20kGy e 30kGy. Para o EVA a 25% foram
preparados 3 filmes para cada dose: 10kGy, 20kGy e 30kGy. Os três filmes restantes, de cada
amostra sem irradiação, foram separados para serem amostras de referência. Nos ensaios de
viscosidade foi observado que a massa molar viscosimétrica média aumentou para todas as
amostras, tanto do EVA a 25% quanto do EVA a 40%, evidenciando a predominância do
efeito de reticulação das macromoléculas. As propriedades de degradação térmica e de índice
de refração não sofreram mudanças significativas após a irradiação. Na análise de
molhabilidade, o ângulo de contato apresentou ligeiro decréscimo no EVA a 40% para a dose
de 20kGy. Na análise de FT-IR o pico de absorção atribuído ao grupo metileno sofreu
modificações marcantes decorrente da radiólise no copolímero para o EVA a 40% e para o
EVA a 25% houve mudanças em todos os picos. Para a segunda parte, as amostras em pellets
foram irradiadas a 250kGy, 500kGy e 1000kGy. Foram analisadas as propriedades de
degradação térmica em atmosferas diferentes e foram observadas mudanças significativas
quando as amostras foram expostas à atmosfera de oxigênio. Para as análises de FT-IR foram
observadas poucas modificações nos picos para todas as amostras. Os resultados mostraram
que é mais favorável o uso do EVA como uma camada intermediária na composição de
embalagens de alimentos por conta da sua boa propriedade de barreira. E para o uso do EVA
em revestimento de cabos elétricos é interessante incorporar ao polímero produtos que
aumentem sua resistência à degradação térmica e a radiação. / Poly (ethylene-co-vinyl acetate), EVA, is a copolymer of olefins family. It is obtained by
chain polymerization by free radical, usually using oxygen and/or organic peroxides to
generate radical initiators of ethylene polymerization and vinyl acetate, under high
temperature and pressure. Its use varies depending on the vinyl acetate content in its
composition and among its utilities are the use in composition of flexible plastic packaging
for irradiated foods and coating for electrical cables. Therefore, it is important to analyze the
gamma radiation effects in these packages. In this study, the investigation of gamma
irradiation effects on EVA was divided into two parts: the first one for lower doses between 5
and 30kGy, used in food irradiation and medical devices radiosterilization, using EVA films
with 25% and 40% of vinyl acetate in its composition. And the second to highest dose (dose
between 250 - 1000kGy), in which the electric cables used in nuclear power plants are
exposed, using EVA with 12%, 25% and 40% in pellet form. For the first part were prepared
12 EVA films at 25% and 18 EVA films at 40% by casting film method, being for EVA of
40% prepared three films for each dose: 5kGy, 10kGy, 15kGy, 20 kGy and 30kGy. For the
EVA at 25% were prepared three films for each dose: 10 kGy, 20 kGy and 30kGy. The
remaining three films of each sample without irradiation were separated for reference
samples. In viscosity experiments it was observed that average viscosimetric molecular
weight increased for all samples, EVA at 25% and 40%, indicating the predominance of
macromolecule reticulation effect. The properties of thermal degradation and refractive index
did not change significantly after irradiation. At the wettability analysis, the contact angle
showed slight decrease in EVA to 40% at the dose of 20 kGy. In the FT-IR analysis, the
absorption peak assigned to methylene group undergoes remarkable changes resulting from
copolymer radiolysis for EVA at 40%; for EVA at 25% were no changes at all peaks. For the
second part, the pellets samples were irradiated with 250kGy, and 500kGy 1000kGy. The
thermal degradation properties were examined in different atmosphere and significant
changes were observed when the samples were exposed to an oxygen atmosphere. For the FTIR
analyzes were observed few changes in peak for all samples. The results showed that it is
more favorable to use EVA as an intermediate layer in the composition of food packaging
because of their good barrier property. And the use of EVA in electrical cable sheathing is
interesting to incorporate into the product polymer to increase its resistance to thermal
degradation and radiation.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/19066 |
Date | 04 March 2016 |
Creators | MEDEIROS, Maria Thalita Siqueira de |
Contributors | http://lattes.cnpq.br/4494328303946478, ARAÚJO, Elmo Silvano de |
Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Tecnologias Energeticas e Nuclear, UFPE, Brasil |
Source Sets | IBICT Brazilian ETDs |
Language | Breton |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds