Synthesis, characterization and properties of zeolite films and membranes

The work presented in this thesis was aimed to synthesize zeolite films in the absence of organic additives to avoid the potentially detrimental calcination procedure. Furthermore, the support surface was seeded with colloidal seed crystals prior to film growth. This technique has previously been used to prepare thin zeolite films. The films were characterized by Scanning electron microscopy (SEM), X-ray diffraction (XRD) and gas permeation experiments. Films of three different types of zeolites were synthesized in this work; FAU-type zeolite, ZSM-5 and zeolite NaA. The thickness of the FAU-type zeolite films could be controlled by varying the synthesis temperature and duration. However, a maximum film thickness was found. Prolonged hydrothermal treatment caused the film thickness to decrease due to the transformation of FAU into zeolite P. The adsorbed seeds were oriented with the <111> pyramid parallel to the surface of the support. During growth, the crystals constituting the films became randomly oriented. The ZSM-5 films were tested as membranes for the separation of butane isomers. The selectivity for n-butane/i-butane had a maximum value of 17.8 at 220°C. Furthermore, the ZSM-5 membranes were found to be catalytically active, converting ethanol into diethylether and ethylene. The growth of silicious species into the porous support during zeolite NaA membrane synthesis was examined. Higher temperatures of synthesis resulted in relatively more growth into the porous support compared to the film growth on top of the support. By using a multi-step synthesis procedure at low temperature, thicker films with less growth into the support could be prepared. / Godkänd; 2001; 20070315 (ysko)

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:ltu-18550
Date January 2001
CreatorsLassinantti, Magdalena
PublisherLuleå tekniska universitet, Luleå
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeLicentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess
RelationLicentiate thesis / Luleå University of Technology, 1402-1757 ; 2001:16

Page generated in 0.0015 seconds